Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F16%3APU119776" target="_blank" >RIV/00216305:26620/16:PU119776 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170

Popis výsledku v původním jazyce

The aim of this analysis was to identify the cause of poor corrosion resistance of final product, after the slight change of heat treatment of initial material. Although the hardness of material prior and after the change was the same, significant difference in microstructure was revealed by microstructural analysis. Change in heat treatment process lead to heterogeneous distribution of precipitates and increase in the precipitate size which caused deterioration in corrosion resistance. Based on the findings, further optimization of heat treatment was suggested. More importantly, initial material inspection based on microstructural analysis, not only mechanical testing, was recommended. recommended.

Název v anglickém jazyce

Influence of Microstructural parameters on the Corrosion Resistance of Aluminium Alloy BS L170

Popis výsledku anglicky

The aim of this analysis was to identify the cause of poor corrosion resistance of final product, after the slight change of heat treatment of initial material. Although the hardness of material prior and after the change was the same, significant difference in microstructure was revealed by microstructural analysis. Change in heat treatment process lead to heterogeneous distribution of precipitates and increase in the precipitate size which caused deterioration in corrosion resistance. Based on the findings, further optimization of heat treatment was suggested. More importantly, initial material inspection based on microstructural analysis, not only mechanical testing, was recommended. recommended.

Druh

O - Ostatní výsledky

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů