Influence of Microstructural Parameters on the Corrosion Resistance of 7075 Aluminium Alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F17%3APU122963" target="_blank" >RIV/00216305:26620/17:PU122963 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.scientificnet/MSF.891.303" target="_blank" >http://www.scientificnet/MSF.891.303</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientificnet/MSF.891.303" target="_blank" >10.4028/www.scientificnet/MSF.891.303</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Influence of Microstructural Parameters on the Corrosion Resistance of 7075 Aluminium Alloy
Popis výsledku v původním jazyce
The aim of this analysis was to identify the cause of poor corrosion resistance of final product, after the slight change of heat treatment of initial material. Although the hardness of material prior and after the change was the same, significant difference in microstructure was revealed by microstructural analysis. Change in heat treatment process lead to heterogeneous distribution of precipitates and increase in the precipitate size which caused deterioration in corrosion resistance. Based on the findings, further optimization of heat treatment was suggested. More importantly, initial material inspection based on microstructural analysis, not only mechanical testing, was recommended. recommended.
Název v anglickém jazyce
Influence of Microstructural Parameters on the Corrosion Resistance of 7075 Aluminium Alloy
Popis výsledku anglicky
The aim of this analysis was to identify the cause of poor corrosion resistance of final product, after the slight change of heat treatment of initial material. Although the hardness of material prior and after the change was the same, significant difference in microstructure was revealed by microstructural analysis. Change in heat treatment process lead to heterogeneous distribution of precipitates and increase in the precipitate size which caused deterioration in corrosion resistance. Based on the findings, further optimization of heat treatment was suggested. More importantly, initial material inspection based on microstructural analysis, not only mechanical testing, was recommended. recommended.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LQ1601" target="_blank" >LQ1601: CEITEC 2020</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Metallography XVI
ISBN
978-3-0357-1018-2
ISSN
0255-5476
e-ISSN
—
Počet stran výsledku
5
Strana od-do
303-307
Název nakladatele
Trans Tech Publications Ltd.
Místo vydání
Switzerland
Místo konání akce
Stará Lesná
Datum konání akce
20. 4. 2016
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—