Enhancement of mechanical properties of 3D-plotted tricalcium phosphate scaffolds by rapid sintering
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F19%3APU133125" target="_blank" >RIV/00216305:26620/19:PU133125 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.mdpi.com/2504-477X/2/3/51" target="_blank" >http://www.mdpi.com/2504-477X/2/3/51</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.jeurceramsoc.2019.05.055" target="_blank" >10.1016/j.jeurceramsoc.2019.05.055</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Enhancement of mechanical properties of 3D-plotted tricalcium phosphate scaffolds by rapid sintering
Popis výsledku v původním jazyce
This work explores the rapid sintering of 3D-plotted tricalcium phosphate (TCP) scaffolds with the aim of getting the on-demand scaffold fabrication closer towards the clinical practice. The sintering trajectories of TCP scaffolds at 1100 and 1200 degrees C show that 10 min of reactive sintering together with a fast heating rate (100 degrees C min(-1)) result in a superior densification without significant grain growth, increasing the compressive strength 1.5-2.5 times. Furthermore, hardness and elastic modulus increase 8 times as compared to conventional sintering. The mechanical performance is not compromised by the formation of alpha-TCP at 1200 degrees C, since it originates by chemical reaction instead of a phase transformation mechanism, avoiding cracking due to crystalline lattice expansion.
Název v anglickém jazyce
Enhancement of mechanical properties of 3D-plotted tricalcium phosphate scaffolds by rapid sintering
Popis výsledku anglicky
This work explores the rapid sintering of 3D-plotted tricalcium phosphate (TCP) scaffolds with the aim of getting the on-demand scaffold fabrication closer towards the clinical practice. The sintering trajectories of TCP scaffolds at 1100 and 1200 degrees C show that 10 min of reactive sintering together with a fast heating rate (100 degrees C min(-1)) result in a superior densification without significant grain growth, increasing the compressive strength 1.5-2.5 times. Furthermore, hardness and elastic modulus increase 8 times as compared to conventional sintering. The mechanical performance is not compromised by the formation of alpha-TCP at 1200 degrees C, since it originates by chemical reaction instead of a phase transformation mechanism, avoiding cracking due to crystalline lattice expansion.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20504 - Ceramics
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of the European Ceramic Society
ISSN
0955-2219
e-ISSN
1873-619X
Svazek periodika
39
Číslo periodika v rámci svazku
14
Stát vydavatele periodika
GB - Spojené království Velké Británie a Severního Irska
Počet stran výsledku
9
Strana od-do
4366-4374
Kód UT WoS článku
000476965000052
EID výsledku v databázi Scopus
2-s2.0-85066436741