Densification of Magnesium Aluminate Spinel Using Manganese and Cobalt Fluoride as Sintering Aids

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F20%3APU136392" target="_blank" >RIV/00216305:26620/20:PU136392 - isvavai.cz</a>

Výsledek na webu

<a href="https://www.mdpi.com/1996-1944/13/1/102" target="_blank" >https://www.mdpi.com/1996-1944/13/1/102</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.3390/ma13010102" target="_blank" >10.3390/ma13010102</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Densification of Magnesium Aluminate Spinel Using Manganese and Cobalt Fluoride as Sintering Aids

Popis výsledku v původním jazyce

Highly dense magnesium aluminate spinel bodies are usually fabricated using pressure-assisted methods, such as spark plasma sintering (SPS), in the presence of lithium fluoride as a sintering aid. The present work investigates whether the addition of transition metal fluorides promotes the sintering of MgAl2O4 bodies during SPS. At the same time, such fluorides can act as a source of optically active dopants. A commercial MgAl2O4 was mixed with 0.5 wt% of LiF, MnF2, and CoF2 and, afterwards, consolidated using SPS at 1400 degrees C. Although MnF2 and CoF2 promote the densification as effectively as LiF, they cause significant grain growth.

Název v anglickém jazyce

Densification of Magnesium Aluminate Spinel Using Manganese and Cobalt Fluoride as Sintering Aids

Popis výsledku anglicky

Highly dense magnesium aluminate spinel bodies are usually fabricated using pressure-assisted methods, such as spark plasma sintering (SPS), in the presence of lithium fluoride as a sintering aid. The present work investigates whether the addition of transition metal fluorides promotes the sintering of MgAl2O4 bodies during SPS. At the same time, such fluorides can act as a source of optically active dopants. A commercial MgAl2O4 was mixed with 0.5 wt% of LiF, MnF2, and CoF2 and, afterwards, consolidated using SPS at 1400 degrees C. Although MnF2 and CoF2 promote the densification as effectively as LiF, they cause significant grain growth.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2020

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials

ISSN

1996-1944

e-ISSN

—

Svazek periodika

13

Číslo periodika v rámci svazku

1

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

10

Strana od-do

„102-1“-„102-10“

Kód UT WoS článku

000515499300102

EID výsledku v databázi Scopus

2-s2.0-85079624806