Femtosecond laser crystallization of YAG in yttrium aluminosilicate glasses

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F00216305%3A26620%2F26%3A0198115" target="_blank" >RIV/00216305:26620/26:0198115 - isvavai.cz</a>

Výsledek na webu

<a href="https://ceramics.onlinelibrary.wiley.com/doi/10.1111/ijag.16710" target="_blank" >https://ceramics.onlinelibrary.wiley.com/doi/10.1111/ijag.16710</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1111/ijag.16710" target="_blank" >10.1111/ijag.16710</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Femtosecond laser crystallization of YAG in yttrium aluminosilicate glasses

Popis výsledku v původním jazyce

This work demonstrates the capability to crystallize YAG via femtosecond pulsed laser. Challenges in using melt-quench glass are shown to restrict glass composition and have not yielded YAG via femtosecond laser crystallization. An alternative glass-making technique was used to fabricate a range of compositions not otherwise possible. Glasses of YAG with added silica in the range of 0-20 mol% were tested under the laser to explore the allowable deviation from stoichiometric YAG. Raman spectroscopy and Electron backscatter diffraction indicated successful fabrication of YAG, and usage of combined excitation emission spectroscopy (CEES) allowed probing of erbium doped compositions.

Název v anglickém jazyce

Femtosecond laser crystallization of YAG in yttrium aluminosilicate glasses

Popis výsledku anglicky

This work demonstrates the capability to crystallize YAG via femtosecond pulsed laser. Challenges in using melt-quench glass are shown to restrict glass composition and have not yielded YAG via femtosecond laser crystallization. An alternative glass-making technique was used to fabricate a range of compositions not otherwise possible. Glasses of YAG with added silica in the range of 0-20 mol% were tested under the laser to explore the allowable deviation from stoichiometric YAG. Raman spectroscopy and Electron backscatter diffraction indicated successful fabrication of YAG, and usage of combined excitation emission spectroscopy (CEES) allowed probing of erbium doped compositions.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20500 - Materials engineering

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

International journal of applied glass science

ISSN

2041-1286

e-ISSN

2041-1294

Svazek periodika

16

Číslo periodika v rámci svazku

4

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

9

Strana od-do

—

Kód UT WoS článku

001498042000001

EID výsledku v databázi Scopus

2-s2.0-105006909581