Vliv tepezlného zpracování na anodické chování Ti-Al-Si vrstev ve fyziologickém roztoku obsahujícího fluoridy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25794787%3A_____%2F08%3A%230000142" target="_blank" >RIV/25794787:_____/08:#0000142 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of heat treatment on anodic behaviour of Ti-Al-Si layers in physiological solution with fluoride additions

Popis výsledku v původním jazyce

Ternary aluminide-silicide layers, capable of protecting titanium surfaces, are interesting because of their easy preparation. Ternary layers created on titanium and on TiAl6V4 alloy exhibit excellent protection against atmospheric oxygen, however, theirresistance in aqueous media has not yet been extensively described in commercial publications. The layers are porous and it is probable that their protective effect may decline because of the fact that the positive effect of low surface oxidation of themost frequently present phase of Ti30Al25Si43 under formation of SiO2 and consequent sealing of pores may not occurs. Annealing of prepared layers promotes sealing of pores as well as hinders migration of ions to interface layer/substrate. At high temperatures superficial oxidation of ternary layers occurs accompanied by formation of SiO2 and Al2O3.

Název v anglickém jazyce

Effect of heat treatment on anodic behaviour of Ti-Al-Si layers in physiological solution with fluoride additions

Popis výsledku anglicky

Ternary aluminide-silicide layers, capable of protecting titanium surfaces, are interesting because of their easy preparation. Ternary layers created on titanium and on TiAl6V4 alloy exhibit excellent protection against atmospheric oxygen, however, theirresistance in aqueous media has not yet been extensively described in commercial publications. The layers are porous and it is probable that their protective effect may decline because of the fact that the positive effect of low surface oxidation of themost frequently present phase of Ti30Al25Si43 under formation of SiO2 and consequent sealing of pores may not occurs. Annealing of prepared layers promotes sealing of pores as well as hinders migration of ions to interface layer/substrate. At high temperatures superficial oxidation of ternary layers occurs accompanied by formation of SiO2 and Al2O3.

Druh

D - Stať ve sborníku

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

First Regional Smyposium on Electrochemistry of South-East Europe

ISBN

978-953-6894-33-8

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

—

Název nakladatele

—

Místo vydání

Croatia

Místo konání akce

Crveni Otok (Chorvatsko)

Datum konání akce

1. 1. 2008

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—