Defects of powder coatings applied on galvanized steel due to hydrogen charging of steel

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25794787%3A_____%2F15%3A%230000603" target="_blank" >RIV/25794787:_____/15:#0000603 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Defects of powder coatings applied on galvanized steel due to hydrogen charging of steel
Popis výsledku v původním jazyce
This case study presents defects do not associated with the actual hot-dip galvanizing process itself but with the additional coating procedure. A multi-coat system of hot dip galvanizing and powder coating is relative frequently used type of surface treatment for various prosucts. In powder coating, many various defects that may form of pinholes or bubbles are a common problem. There are many reasons for this defects. This paper presents failure analysis methodology and the step-by-step approach to theparticular case study.
Název v anglickém jazyce
Defects of powder coatings applied on galvanized steel due to hydrogen charging of steel
Popis výsledku anglicky
This case study presents defects do not associated with the actual hot-dip galvanizing process itself but with the additional coating procedure. A multi-coat system of hot dip galvanizing and powder coating is relative frequently used type of surface treatment for various prosucts. In powder coating, many various defects that may form of pinholes or bubbles are a common problem. There are many reasons for this defects. This paper presents failure analysis methodology and the step-by-step approach to theparticular case study.

Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění
2015
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)