Depreciation of powder coating applied on zinc electroplated steel due to hydrogen charging of steel

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25794787%3A_____%2F16%3AN0000013" target="_blank" >RIV/25794787:_____/16:N0000013 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Depreciation of powder coating applied on zinc electroplated steel due to hydrogen charging of steel
Popis výsledku v původním jazyce
This case study presents defects associated with the actual zinc galvanizing process itself but not with the additional coating procedure. A multi-coat system of zinc galvanizing and powder coating is relative frequently used type of surface treatment for various products. In powder coating many various defects may form of pinholes or bubbles are a common problem. There are many reasons for this defect. This paper presents failure analysis methodology and the step-by-step approach to the particular case study.
Název v anglickém jazyce
Depreciation of powder coating applied on zinc electroplated steel due to hydrogen charging of steel
Popis výsledku anglicky
This case study presents defects associated with the actual zinc galvanizing process itself but not with the additional coating procedure. A multi-coat system of zinc galvanizing and powder coating is relative frequently used type of surface treatment for various products. In powder coating many various defects may form of pinholes or bubbles are a common problem. There are many reasons for this defect. This paper presents failure analysis methodology and the step-by-step approach to the particular case study.

Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)