Fatigue properties of a low alloy 42SiCr steel heat treated by quenching and partitioning process
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F11%3A%230000275" target="_blank" >RIV/25797000:_____/11:#0000275 - isvavai.cz</a>
Výsledek na webu
<a href="http://www.sciencedirect.com/science/article/pii/S187770581100734X" target="_blank" >http://www.sciencedirect.com/science/article/pii/S187770581100734X</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1016/j.proeng.2011.04.546" target="_blank" >10.1016/j.proeng.2011.04.546</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Fatigue properties of a low alloy 42SiCr steel heat treated by quenching and partitioning process
Popis výsledku v původním jazyce
An experimental low alloy 42SiCr steel has been developed. Well balanced properties, i.e. strength about 2000 MPa and ductility more than 10 ? 15%, were achieved by an application of advanced heat treatment methods like Q-P (quenching and partitioning) process. The aim of this study was to investigate fatigue properties of the 42SiCr steel treated using the Q-P process. Results of fatigue experiments are presented with respect to the basic material state and after traditional heat treatment ? quenchingand tempering. Fatigue damage initiation mechanisms and connections between fatigue properties and microstructure are discussed.
Název v anglickém jazyce
Fatigue properties of a low alloy 42SiCr steel heat treated by quenching and partitioning process
Popis výsledku anglicky
An experimental low alloy 42SiCr steel has been developed. Well balanced properties, i.e. strength about 2000 MPa and ductility more than 10 ? 15%, were achieved by an application of advanced heat treatment methods like Q-P (quenching and partitioning) process. The aim of this study was to investigate fatigue properties of the 42SiCr steel treated using the Q-P process. Results of fatigue experiments are presented with respect to the basic material state and after traditional heat treatment ? quenchingand tempering. Fatigue damage initiation mechanisms and connections between fatigue properties and microstructure are discussed.
Klasifikace
Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/1M06032" target="_blank" >1M06032: VÝZKUMNÉ CENTRUM TVÁŘECÍCH TECHNOLOGIÍ</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Procedia Engineering
ISSN
1877-7058
e-ISSN
—
Svazek periodika
10
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
NL - Nizozemsko
Počet stran výsledku
6
Strana od-do
3310-3315
Kód UT WoS článku
000300451303055
EID výsledku v databázi Scopus
—