THE SENSITIVITY OF 42SiCr STEEL TO INCLUSIONS UNDER FATIGUE LOADING FOR THREE DIFFERENT WAYS OF HEAT TREATMENT
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25797000%3A_____%2F12%3A%230000286" target="_blank" >RIV/25797000:_____/12:#0000286 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/25797000:_____/12:#0000363
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
THE SENSITIVITY OF 42SiCr STEEL TO INCLUSIONS UNDER FATIGUE LOADING FOR THREE DIFFERENT WAYS OF HEAT TREATMENT
Popis výsledku v původním jazyce
The aim of this work was the interpretation of results of fatigue tests of low alloy 42SiCr steel. Three different types of heat treatment conditions were compared: (i) as received hot rolled material, (ii) classically heat treated material (quenched andtempered) and (iii) heat treated material using advanced quenching and partitioning (Q-P) process. The results of fatigue tests in combination with fractographical analysis showed significant differences concerning effects of inclusions on fatigue crackinitiation evaluated as a dependence on the type of heat treatment of the samples. The influence of inclusions was evaluated by Murakami´s model (Murakami and Endo, 1994 [1]). This influence was compared with the difference of real fatigue life and expected fatigue life from Wöhler curve.
Název v anglickém jazyce
THE SENSITIVITY OF 42SiCr STEEL TO INCLUSIONS UNDER FATIGUE LOADING FOR THREE DIFFERENT WAYS OF HEAT TREATMENT
Popis výsledku anglicky
The aim of this work was the interpretation of results of fatigue tests of low alloy 42SiCr steel. Three different types of heat treatment conditions were compared: (i) as received hot rolled material, (ii) classically heat treated material (quenched andtempered) and (iii) heat treated material using advanced quenching and partitioning (Q-P) process. The results of fatigue tests in combination with fractographical analysis showed significant differences concerning effects of inclusions on fatigue crackinitiation evaluated as a dependence on the type of heat treatment of the samples. The influence of inclusions was evaluated by Murakami´s model (Murakami and Endo, 1994 [1]). This influence was compared with the difference of real fatigue life and expected fatigue life from Wöhler curve.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JL - Únava materiálu a lomová mechanika
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/1M06032" target="_blank" >1M06032: VÝZKUMNÉ CENTRUM TVÁŘECÍCH TECHNOLOGIÍ</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2012
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Conference METAL 2012 Proceedings
ISBN
978-80-87294-31-4
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
—
Název nakladatele
Tanger Ltd.
Místo vydání
—
Místo konání akce
Brno, ČR
Datum konání akce
23. 5. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—