Creep and Fracture Behaviour of Dissimilar P91/P23 WeldsCreep and Fracture Behaviour of Dissimilar P91/P23 Welds

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25870807%3A_____%2F09%3A%230000158" target="_blank" >RIV/25870807:_____/09:#0000158 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Creep and Fracture Behaviour of Dissimilar P91/P23 WeldsCreep and Fracture Behaviour of Dissimilar P91/P23 Welds

Popis výsledku v původním jazyce

Cross weld creep rupture tests have been conducted on dissimilar P91/P23 welds at temperatures 500, 550 and 600°C up to 3x104 hours. Welds A and B were manufactured by MMA process using low alloy (Thyssen Cr2WV) and high alloy (E CrMo 91B) consumables, respectively. This paper describes the effect of creep test variables on the failure mechanisms of alternative weld designs. The fracture behaviour of creep ruptured specimens was investigated by using optical and electron microscopy. Furthermore, hardness profiles were evaluated on longitudinal sections through the ruptured cross weld test pieces.

Název v anglickém jazyce

Creep and Fracture Behaviour of Dissimilar P91/P23 WeldsCreep and Fracture Behaviour of Dissimilar P91/P23 Welds

Popis výsledku anglicky

Cross weld creep rupture tests have been conducted on dissimilar P91/P23 welds at temperatures 500, 550 and 600°C up to 3x104 hours. Welds A and B were manufactured by MMA process using low alloy (Thyssen Cr2WV) and high alloy (E CrMo 91B) consumables, respectively. This paper describes the effect of creep test variables on the failure mechanisms of alternative weld designs. The fracture behaviour of creep ruptured specimens was investigated by using optical and electron microscopy. Furthermore, hardness profiles were evaluated on longitudinal sections through the ruptured cross weld test pieces.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/OC%20099" target="_blank" >OC 099: Creepové chování a mikrostrukturní stabilita nových 9-12%Cr ocelí pro elektrárny s nadkritickými parametry páry</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Mechanics and Materials in Design

ISBN

972-8826-11-7

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

—

Název nakladatele

Claret ? Companhia Grafica do Norte

Místo vydání

Avintes, Portugal

Místo konání akce

Porto, Portugal

Datum konání akce

1. 1. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—