The use of numerical simulations to obtain the basic knowledge about casting process of heavy circular ingot
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F25870807%3A_____%2F19%3AN0000047" target="_blank" >RIV/25870807:_____/19:N0000047 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.metalconference.eu/files/uploads/02//METAL2019_Conference_Proceedings_Content.pdf" target="_blank" >https://www.metalconference.eu/files/uploads/02//METAL2019_Conference_Proceedings_Content.pdf</a>
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The use of numerical simulations to obtain the basic knowledge about casting process of heavy circular ingot
Popis výsledku v původním jazyce
During the casting of heavier ingots, internal porosity occurs during solidification due to shrinkage of the cast metal. Porosity, or non-metal-filled areas, is up to several centimeters inside large ingots. The present work deals with the study of physical-metallurgical parameters of casting a large circular ingot, leading to the elimination of porosity. Which was done using the numerical software Magma 5.4. In order to find the most suitable casting conditions, the planned experiment method called DoE was also partially used. Particular attention was paid to casting speed with investigation and finding the most suitable casting temperature. For the basic variant cast in the Magma software, an initial investigation of the temperature field and voltage state during the ingot cooling in the numerical software Forge NxT 2.1 was performed.
Název v anglickém jazyce
The use of numerical simulations to obtain the basic knowledge about casting process of heavy circular ingot
Popis výsledku anglicky
During the casting of heavier ingots, internal porosity occurs during solidification due to shrinkage of the cast metal. Porosity, or non-metal-filled areas, is up to several centimeters inside large ingots. The present work deals with the study of physical-metallurgical parameters of casting a large circular ingot, leading to the elimination of porosity. Which was done using the numerical software Magma 5.4. In order to find the most suitable casting conditions, the planned experiment method called DoE was also partially used. Particular attention was paid to casting speed with investigation and finding the most suitable casting temperature. For the basic variant cast in the Magma software, an initial investigation of the temperature field and voltage state during the ingot cooling in the numerical software Forge NxT 2.1 was performed.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/EF17_049%2F0008399" target="_blank" >EF17_049/0008399: Rozvoj mezisektorové spolupráce RMTVC s aplikační sférou v oblasti výzkumu progresivních a inovací klasických kovových materiálů a technologií s využitím metod modelování</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2019
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Metal 2019
ISBN
978-80-87294-92-5
ISSN
—
e-ISSN
—
Počet stran výsledku
7
Strana od-do
168-174
Název nakladatele
Tanger Ltd.
Místo vydání
Ostrava
Místo konání akce
Brno
Datum konání akce
22. 5. 2019
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
999