Vývoj mikrostruktury během rekrystalizace slitiny MoNiCr
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F06%3A%230000085" target="_blank" >RIV/26316919:_____/06:#0000085 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Microstructure Evolution during Recrystallization of MoNiCr alloy
Popis výsledku v původním jazyce
This research provides an attempt to achieve uniform grain structure by recrystallization process from different hot and cold-working conditions followed by various annealing in NiMoCr alloy. The different structure would result in high temperature mechanical properties such as ductility, fatigue, and creep strength. The microstructural changes results from all tested programs were investigated by an optical microscope. The results showed the uniformity of the recrystallized structure strongly relatingto the amount of reduction during hot working and period of annealing time. It was found that the uniformity of recrystallized structure increased with a higher amount of deformation and longer annealing time. Furthermore, the results illustrated that the recrystallized structure on the surface layer was finer than the interior of the sample. This could be due to the recrystallization occurring close to the specimen surface, which was influenced by a much higher degree of deformation and
Název v anglickém jazyce
Microstructure Evolution during Recrystallization of MoNiCr alloy
Popis výsledku anglicky
This research provides an attempt to achieve uniform grain structure by recrystallization process from different hot and cold-working conditions followed by various annealing in NiMoCr alloy. The different structure would result in high temperature mechanical properties such as ductility, fatigue, and creep strength. The microstructural changes results from all tested programs were investigated by an optical microscope. The results showed the uniformity of the recrystallized structure strongly relatingto the amount of reduction during hot working and period of annealing time. It was found that the uniformity of recrystallized structure increased with a higher amount of deformation and longer annealing time. Furthermore, the results illustrated that the recrystallized structure on the surface layer was finer than the interior of the sample. This could be due to the recrystallization occurring close to the specimen surface, which was influenced by a much higher degree of deformation and
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JP - Průmyslové procesy a zpracování
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/GA106%2F06%2F1352" target="_blank" >GA106/06/1352: Materiálové vlastnosti modifikovaných Ni superslitin</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2006
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Program and book of abstracts 14. conference on materials and technology
ISBN
978-961-91448-6-2
ISSN
—
e-ISSN
—
Počet stran výsledku
1
Strana od-do
—
Název nakladatele
Inštitut za kovinske materiale in technologie, Ljubljana
Místo vydání
Portorož
Místo konání akce
Portorož
Datum konání akce
1. 1. 2006
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—