Vliv podmínek válcování a tepelného zpracování na mikrostrukturu tepelně odolné sslitiny niklu

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F07%3A%230000091" target="_blank" >RIV/26316919:_____/07:#0000091 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Effect of Rolling and Heat-treatment Conditions on Microstructure in Heat-resisting Nickel Alloy

Popis výsledku v původním jazyce

This research provides an attempt to achieve uniform grain structure by recrystallization process from different hot and cold-working conditions followed by various annealing in NiMoCr alloy. The different structure would result in high temperature mechanicalproperties such as ductility, fatigue, and creep strength. The microstructural changes results from all tested programs were investigated by an optical microscope. The results showed the uniformity of the recrystallized structure strongly relating to the amount of reduction during hot working and period of annealing time. It was found that the uniformity of recrystallized structure increased with a higher amount of deformation and longe annealing time.

Název v anglickém jazyce

Effect of Rolling and Heat-treatment Conditions on Microstructure in Heat-resisting Nickel Alloy

Popis výsledku anglicky

This research provides an attempt to achieve uniform grain structure by recrystallization process from different hot and cold-working conditions followed by various annealing in NiMoCr alloy. The different structure would result in high temperature mechanicalproperties such as ductility, fatigue, and creep strength. The microstructural changes results from all tested programs were investigated by an optical microscope. The results showed the uniformity of the recrystallized structure strongly relating to the amount of reduction during hot working and period of annealing time. It was found that the uniformity of recrystallized structure increased with a higher amount of deformation and longe annealing time.

Druh

D - Stať ve sborníku

CEP obor

JP - Průmyslové procesy a zpracování

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F06%2F1352" target="_blank" >GA106/06/1352: Materiálové vlastnosti modifikovaných Ni superslitin</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2007

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

28th Sampe Europe

ISBN

978-3-9522677-5-2

ISSN

—

e-ISSN

—

Počet stran výsledku

12

Strana od-do

—

Název nakladatele

Sampe Europe

Místo vydání

Paříž

Místo konání akce

Paříž

Datum konání akce

1. 1. 2007

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—