Innovative Concepts for Hot Stamping Process

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F11%3A%230000307" target="_blank" >RIV/26316919:_____/11:#0000307 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Innovative Concepts for Hot Stamping Process

Popis výsledku v původním jazyce

Hot stamping is typically used for manufacturing car body parts. This process allows forming parts with high strength. Thanks to hot deformation and rapid cooling, shaped parts with martensite microstructure and high yield and ultimate strengths are obtained. this paper provides an introduction to a new hot stamping process used together with the Q-P process (quenching and partitioning) for processing of high strength low alloy steels. By this procedure and by controlling the microstructure development,high strength exceeding 2000 MPa and elongation over 10% can be achieved. A steel containing 0,43% C, 0,59 - 1,17% manganese and 2 - 2,6% silicon was used for this experiment. FEM analysis was carried out to find hot stamping parameters for selected chemical compositions and sheet thicknesses. The results formed a basis of experimental work. The work consisted in material-technological modelling using a thermomechanical simulator. The primary goal of the experiment +was to test the comb

Název v anglickém jazyce

Innovative Concepts for Hot Stamping Process

Popis výsledku anglicky

Hot stamping is typically used for manufacturing car body parts. This process allows forming parts with high strength. Thanks to hot deformation and rapid cooling, shaped parts with martensite microstructure and high yield and ultimate strengths are obtained. this paper provides an introduction to a new hot stamping process used together with the Q-P process (quenching and partitioning) for processing of high strength low alloy steels. By this procedure and by controlling the microstructure development,high strength exceeding 2000 MPa and elongation over 10% can be achieved. A steel containing 0,43% C, 0,59 - 1,17% manganese and 2 - 2,6% silicon was used for this experiment. FEM analysis was carried out to find hot stamping parameters for selected chemical compositions and sheet thicknesses. The results formed a basis of experimental work. The work consisted in material-technological modelling using a thermomechanical simulator. The primary goal of the experiment +was to test the comb

Druh

D - Stať ve sborníku

CEP obor

JP - Průmyslové procesy a zpracování

OECD FORD obor

—

Projekt

<a href="/cs/project/1M06032" target="_blank" >1M06032: VÝZKUMNÉ CENTRUM TVÁŘECÍCH TECHNOLOGIÍ</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

10th International Conference on The Technology of Plasticity, ICTP 2011, Special Edition

ISBN

978-3-514-00784-0

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

423-428

Název nakladatele

Wiley-VCH Verlag GmbH & Co.

Místo vydání

Weinheim, Germany

Místo konání akce

Aachen, Germany

Datum konání akce

25. 8. 2011

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—