Innovative concepts for hot stamping process

Popis výsledku v původním jazyce

Hot Stamping is typically used for manufacturing car body parts. This process allows forming parts with high strength. Thanks to hot deformation and rapid cooling, shaped parts with martensite and high yield and ultimate strengths are obtained. This paper propose an introduction to a new hot stamping process used together with the Q-P process (quenching and partitioning) for processing of high strength low alloy steels. By this procedure and by controlling the microstructure development, high strength exceeding 2000 MPa and elongation over 10% can be achieved. A steel containing 0.43% C, 0.59 - 17 % manganese and 2 - 2.6 % silicon was used for this experiment. FEM analysis was carried out to find hot stamping parameters for selected chemical compositions and sheet thicknesses.

Název v anglickém jazyce

Innovative concepts for hot stamping process

Popis výsledku anglicky

Hot Stamping is typically used for manufacturing car body parts. This process allows forming parts with high strength. Thanks to hot deformation and rapid cooling, shaped parts with martensite and high yield and ultimate strengths are obtained. This paper propose an introduction to a new hot stamping process used together with the Q-P process (quenching and partitioning) for processing of high strength low alloy steels. By this procedure and by controlling the microstructure development, high strength exceeding 2000 MPa and elongation over 10% can be achieved. A steel containing 0.43% C, 0.59 - 17 % manganese and 2 - 2.6 % silicon was used for this experiment. FEM analysis was carried out to find hot stamping parameters for selected chemical compositions and sheet thicknesses.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2011

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Steel Research International, Special Edition

ISSN

1611-3683

e-ISSN

—

Svazek periodika

Neuveden

Číslo periodika v rámci svazku

—

Stát vydavatele periodika

DE - Spolková republika Německo

Počet stran výsledku

6

Strana od-do

423-428

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—