Enhancing Corrosion Resistance of Chromium-Nickel Stainless Steel Equipment

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F14%3A%230000521" target="_blank" >RIV/26316919:_____/14:#0000521 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Enhancing Corrosion Resistance of Chromium-Nickel Stainless Steel Equipment

Popis výsledku v původním jazyce

The paper discusses the problem of recurrent corrosion of casing of metal detectors used in food industry. The detector casing is fabricated by welding sheets of X5CrNi18-10 stainless steel. The detectors in service suffered non-uniform spot corrosion. The likely cause of the corrosion attack was the accumulated contamination of the detector surface with cleaning and disinfecting agents containing chlorine. The sheet surfaces of the original detectors were shot-blasted. After the sheet finishing processwas changed to grinding and minor design changes were made, the corrosion resistance of the detector casing improved. The enhanced corrosion resistance of the detectors with ground surfaces was confirmed by salt spray tests. The use of the modified detectors then led to a lower number of complaints about the devices.

Název v anglickém jazyce

Enhancing Corrosion Resistance of Chromium-Nickel Stainless Steel Equipment

Popis výsledku anglicky

The paper discusses the problem of recurrent corrosion of casing of metal detectors used in food industry. The detector casing is fabricated by welding sheets of X5CrNi18-10 stainless steel. The detectors in service suffered non-uniform spot corrosion. The likely cause of the corrosion attack was the accumulated contamination of the detector surface with cleaning and disinfecting agents containing chlorine. The sheet surfaces of the original detectors were shot-blasted. After the sheet finishing processwas changed to grinding and minor design changes were made, the corrosion resistance of the detector casing improved. The enhanced corrosion resistance of the detectors with ground surfaces was confirmed by salt spray tests. The use of the modified detectors then led to a lower number of complaints about the devices.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/ED2.1.00%2F03.0077" target="_blank" >ED2.1.00/03.0077: Západočeské materiálově metalurgické centrum</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Přínos metalografie pro řešení výrobních problémů

ISBN

978-80-01-05474-1

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

184-190

Název nakladatele

Česká technika - nakladatelství ČVUT v Praze

Místo vydání

Praha

Místo konání akce

Lázně Libverda

Datum konání akce

1. 1. 2014

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—