Mechanical properties of laminated steel-based composite materials fabricated by hot rolling
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F17%3AN0000007" target="_blank" >RIV/26316919:_____/17:N0000007 - isvavai.cz</a>
Výsledek na webu
<a href="http://mit.imt.si/Revija/izvodi/mit174/kubina.pdf" target="_blank" >http://mit.imt.si/Revija/izvodi/mit174/kubina.pdf</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.17222/mit.2015.227" target="_blank" >10.17222/mit.2015.227</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Mechanical properties of laminated steel-based composite materials fabricated by hot rolling
Popis výsledku v původním jazyce
The fabrication of laminated steel composites by hot rolling is described. Composite sandwiches were made from martensitic stainless tool steel with an increased nitrogen content and from standard AISI 304 steel using 3 to 7 layers. The maximum strength of the martensitic steel was 1370 MPa. The composite sheets had strengths in the range 950-1200 MPa, depending on the number of layers and the proportion of the steels. A metallographic observation of the fractures revealed that the first occurrence was fracture in the martensitic steel layers, followed by deformation of the layers of tough austenitic AISI 304 steel. The notch toughness values were the highest when the notch was oriented from the sheet surface to the sheet interior.
Název v anglickém jazyce
Mechanical properties of laminated steel-based composite materials fabricated by hot rolling
Popis výsledku anglicky
The fabrication of laminated steel composites by hot rolling is described. Composite sandwiches were made from martensitic stainless tool steel with an increased nitrogen content and from standard AISI 304 steel using 3 to 7 layers. The maximum strength of the martensitic steel was 1370 MPa. The composite sheets had strengths in the range 950-1200 MPa, depending on the number of layers and the proportion of the steels. A metallographic observation of the fractures revealed that the first occurrence was fracture in the martensitic steel layers, followed by deformation of the layers of tough austenitic AISI 304 steel. The notch toughness values were the highest when the notch was oriented from the sheet surface to the sheet interior.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LO1412" target="_blank" >LO1412: Rozvoj Západočeského materiálově metalurgického Centra</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
MATERIALI IN TEHNOLOGIJE
ISSN
1580-2949
e-ISSN
1580-3414
Svazek periodika
51
Číslo periodika v rámci svazku
4
Stát vydavatele periodika
SI - Slovinská republika
Počet stran výsledku
5
Strana od-do
557-561
Kód UT WoS článku
000408399700001
EID výsledku v databázi Scopus
—