Strengthening and Thermally Activated Processes in an AX61/Saffil Metal Matrix Composite
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F20%3AN0000014" target="_blank" >RIV/26316919:_____/20:N0000014 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216208:11320/20:10420682
Výsledek na webu
<a href="https://www.mdpi.com/2073-4352/10/6/466/htm" target="_blank" >https://www.mdpi.com/2073-4352/10/6/466/htm</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/cryst10060466" target="_blank" >10.3390/cryst10060466</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Strengthening and Thermally Activated Processes in an AX61/Saffil Metal Matrix Composite
Popis výsledku v původním jazyce
AX61 magnesium alloy was reinforced with short Saffil fibres using squeeze cast technology. Samples were cut from the casting in two directions: parallel and perpendicular to the fibre plane. Samples were deformed in compression at various temperatures from room temperature to 300 degrees C. Various strengthening mechanisms such as load transfer, increased dislocation density, Orowan and Hall-Petch strengthening were analysed. During deformation, the stress relaxation tests were subsequently performed. The relaxation curves were evaluated with respect to Li and Feltham equations with the aim to find stress components in matrix and parameters of the thermally activated process(es).
Název v anglickém jazyce
Strengthening and Thermally Activated Processes in an AX61/Saffil Metal Matrix Composite
Popis výsledku anglicky
AX61 magnesium alloy was reinforced with short Saffil fibres using squeeze cast technology. Samples were cut from the casting in two directions: parallel and perpendicular to the fibre plane. Samples were deformed in compression at various temperatures from room temperature to 300 degrees C. Various strengthening mechanisms such as load transfer, increased dislocation density, Orowan and Hall-Petch strengthening were analysed. During deformation, the stress relaxation tests were subsequently performed. The relaxation curves were evaluated with respect to Li and Feltham equations with the aim to find stress components in matrix and parameters of the thermally activated process(es).
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
—
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
CRYSTALS
ISSN
2073-4352
e-ISSN
2073-4352
Svazek periodika
10
Číslo periodika v rámci svazku
6
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
13
Strana od-do
nestránkováno
Kód UT WoS článku
000551210200001
EID výsledku v databázi Scopus
2-s2.0-85086040527