MICROSTRUCTURAL OBSERVATIONS OF AM DEPOSITED 15-5PH-STELLITE SAMPLE
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F21%3AN0000003" target="_blank" >RIV/26316919:_____/21:N0000003 - isvavai.cz</a>
Výsledek na webu
<a href="https://www.mmscience.eu/journal/issues/march-2021/articles/microstructural-observations-of-am-deposited-15-5ph-stellite-sample" target="_blank" >https://www.mmscience.eu/journal/issues/march-2021/articles/microstructural-observations-of-am-deposited-15-5ph-stellite-sample</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.17973/MMSJ.2021_03_2021003" target="_blank" >10.17973/MMSJ.2021_03_2021003</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
MICROSTRUCTURAL OBSERVATIONS OF AM DEPOSITED 15-5PH-STELLITE SAMPLE
Popis výsledku v původním jazyce
In the present work AM (Additive Manufacturing) was used to create a build on a baseplate in order to find out its ability to repair damaged parts (from baseplate material). The material of the baseplate was AKT1TD martensitic steel used in the aviation and energy industry. The steel could suffer from corrosion and erosion, and AM could be the solution for the damaged parts repairing. As a first step, a material similar to the baseplate was deposited. After that, a deposition of a stellite protective layer took place to increase the corrosion-erosion resistance. The whole build was observed by OM (optical microscopy) and SEM (scanning electron microscopy) to find out the quality of deposition.
Název v anglickém jazyce
MICROSTRUCTURAL OBSERVATIONS OF AM DEPOSITED 15-5PH-STELLITE SAMPLE
Popis výsledku anglicky
In the present work AM (Additive Manufacturing) was used to create a build on a baseplate in order to find out its ability to repair damaged parts (from baseplate material). The material of the baseplate was AKT1TD martensitic steel used in the aviation and energy industry. The steel could suffer from corrosion and erosion, and AM could be the solution for the damaged parts repairing. As a first step, a material similar to the baseplate was deposited. After that, a deposition of a stellite protective layer took place to increase the corrosion-erosion resistance. The whole build was observed by OM (optical microscopy) and SEM (scanning electron microscopy) to find out the quality of deposition.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/TN01000007" target="_blank" >TN01000007: Národní centrum pro energetiku</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2021
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
MM SCIENCE JOURNAL
ISSN
1803-1269
e-ISSN
1805-0476
Svazek periodika
2021
Číslo periodika v rámci svazku
March
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
6
Strana od-do
4316-4321
Kód UT WoS článku
000634572700013
EID výsledku v databázi Scopus
2-s2.0-85102766044