EVOLUTION OF MICROSTRUCTURE AND EMBRITTLEMENT DURING THE TEMPERING PROCESS IN SiCrCu MEDIUM C STEELS

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26316919%3A_____%2F23%3AN0000027" target="_blank" >RIV/26316919:_____/23:N0000027 - isvavai.cz</a>

Výsledek na webu

<a href="http://mater-tehnol.si/index.php/MatTech/article/view/744" target="_blank" >http://mater-tehnol.si/index.php/MatTech/article/view/744</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.17222/mit.2023.744" target="_blank" >10.17222/mit.2023.744</a>

Jazyk výsledku

angličtina

Název v původním jazyce

EVOLUTION OF MICROSTRUCTURE AND EMBRITTLEMENT DURING THE TEMPERING PROCESS IN SiCrCu MEDIUM C STEELS

Popis výsledku v původním jazyce

The effect of Cu and Si contents on the evolution of embrittlement during a heat treatment consisting of quenching into an oil bath and tempering in the range 200-500 degrees C was investigated in medium-carbon steels with 0.48 w/% and 0.57 w/% of C. The results showed that the higher silicon content shifted the tempered martensite embrittlement to higher tempering temperatures. The steels alloyed with Cu had lower notch-toughness values, which worsened with increasing tempering temperature compared to the Cu- free samples. In the investigated tempering temperature range, the following microstructural changes occurred: formation of transition carbides, decomposition of retained austenite, and precipitation of cementite and Cu-particles.

Název v anglickém jazyce

EVOLUTION OF MICROSTRUCTURE AND EMBRITTLEMENT DURING THE TEMPERING PROCESS IN SiCrCu MEDIUM C STEELS

Popis výsledku anglicky

The effect of Cu and Si contents on the evolution of embrittlement during a heat treatment consisting of quenching into an oil bath and tempering in the range 200-500 degrees C was investigated in medium-carbon steels with 0.48 w/% and 0.57 w/% of C. The results showed that the higher silicon content shifted the tempered martensite embrittlement to higher tempering temperatures. The steels alloyed with Cu had lower notch-toughness values, which worsened with increasing tempering temperature compared to the Cu- free samples. In the investigated tempering temperature range, the following microstructural changes occurred: formation of transition carbides, decomposition of retained austenite, and precipitation of cementite and Cu-particles.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/EF16_019%2F0000836" target="_blank" >EF16_019/0000836: Výzkum pokročilých ocelí s unikátními vlastnostmi</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

MATERIALI IN TEHNOLOGIJE

ISSN

1580-2949

e-ISSN

1580-3414

Svazek periodika

57

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

SI - Slovinská republika

Počet stran výsledku

12

Strana od-do

233-240

Kód UT WoS článku

001008264200003

EID výsledku v databázi Scopus

2-s2.0-85167893664