Studie pomalého cyklického zatěžování nerezové oceli a-y duplex pomocí difrakce neutronů

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F06%3A%230000039" target="_blank" >RIV/26722445:_____/06:#0000039 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

In situ neutron diffraction study of the low cycle fatigue of the a-y duplex stainless steel

Popis výsledku v původním jazyce

In duplex stainless steels, significant thermal stresses are generated during the cooling from the homogenization temperature due to different thermal expansion coefficients of the austenitic and ferritic phases. The results of the in situ neutron diffraction examination of the evolution of the internal stresses during the low cycle fatigue in the SAF 2507 duplex stainless steel are reported. Stress response of both constituent components resulting from the load sharing between austenitic and ferritic grains was measured. It was found that the initial thermal residual stresses were relaxed rapidly at the beginning of the cyclic loading. Whereas initial hardening was identified in both phases, the subsequent fatigue softening was fully attributed to theaustenitic phase.

Název v anglickém jazyce

In situ neutron diffraction study of the low cycle fatigue of the a-y duplex stainless steel

Popis výsledku anglicky

In duplex stainless steels, significant thermal stresses are generated during the cooling from the homogenization temperature due to different thermal expansion coefficients of the austenitic and ferritic phases. The results of the in situ neutron diffraction examination of the evolution of the internal stresses during the low cycle fatigue in the SAF 2507 duplex stainless steel are reported. Stress response of both constituent components resulting from the load sharing between austenitic and ferritic grains was measured. It was found that the initial thermal residual stresses were relaxed rapidly at the beginning of the cyclic loading. Whereas initial hardening was identified in both phases, the subsequent fatigue softening was fully attributed to theaustenitic phase.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2006

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Physica B: Condensed Matter

ISSN

0921-4526

e-ISSN

—

Svazek periodika

385-386

Číslo periodika v rámci svazku

Part 1

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

3

Strana od-do

597-599

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—