Evolution of ω phase during heating of metastable β titanium alloy Ti–15Mo
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F18%3AN0000002" target="_blank" >RIV/26722445:_____/18:N0000002 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.1007/s10853-017-1519-2" target="_blank" >http://dx.doi.org/10.1007/s10853-017-1519-2</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.1007/s10853-017-1519-2" target="_blank" >10.1007/s10853-017-1519-2</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Evolution of ω phase during heating of metastable β titanium alloy Ti–15Mo
Popis výsledku v původním jazyce
Evolution of ω phase during heating of metastable β titanium alloy Ti–15Mo was investigated in situ during heating by electrical resistance measurements and accompanied by transmission electron microscopy. Different heating rates were employed aiming to determine kinetics of occurring phase transformations. Sharp change of temperature dependence of electrical resistance caused by complete dissolution of ω phase was observed at 560 ∘C independently of heating rate. Majority of ωiso particles revert back to β phase at 560 ∘C; therefore, they are not direct precursors of α precipitation during continuous heating.
Název v anglickém jazyce
Evolution of ω phase during heating of metastable β titanium alloy Ti–15Mo
Popis výsledku anglicky
Evolution of ω phase during heating of metastable β titanium alloy Ti–15Mo was investigated in situ during heating by electrical resistance measurements and accompanied by transmission electron microscopy. Different heating rates were employed aiming to determine kinetics of occurring phase transformations. Sharp change of temperature dependence of electrical resistance caused by complete dissolution of ω phase was observed at 560 ∘C independently of heating rate. Majority of ωiso particles revert back to β phase at 560 ∘C; therefore, they are not direct precursors of α precipitation during continuous heating.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/LQ1603" target="_blank" >LQ1603: Výzkum pro SUSEN</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Journal of Materials Science
ISSN
0022-2461
e-ISSN
1573-4803
Svazek periodika
53
Číslo periodika v rámci svazku
1
Stát vydavatele periodika
US - Spojené státy americké
Počet stran výsledku
9
Strana od-do
837-845
Kód UT WoS článku
000412900500060
EID výsledku v databázi Scopus
2-s2.0-85028976256