3D analysis of macrosegregation in twin-roll cast AA3003 alloy before and after heat treatment

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F18%3AN0000167" target="_blank" >RIV/26722445:_____/18:N0000167 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216208:11320/18:10390397

Výsledek na webu

<a href="https://material.karlov.mff.cuni.cz/people/pokova/www/Bajer_Metal2018.pdf" target="_blank" >https://material.karlov.mff.cuni.cz/people/pokova/www/Bajer_Metal2018.pdf</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

3D analysis of macrosegregation in twin-roll cast AA3003 alloy before and after heat treatment

Popis výsledku v původním jazyce

Twin-roll casting allows production of sheets and strips with required thickness without subsequent homogenization or hot rolling and therefore has a high potential for industrial applications. One of the drawbacks of this method is a formation of inhomogeneous structure with central segregation. Sheet prepared from 3003 aluminum alloy with 1 wt.% Mn, 0.2 wt.% Fe, 0.5 wt.% Si, 0.2 wt.% Cu and small addition of Zr (0.2 wt.%) and Cr (0.1 wt.%) was studied by X-ray computed tomography. Segregations in the material form as manganese, iron and silicon rich channels spread in the rolling direction. The material annealed at 450 °C exhibits diffusion of alloying elements from segregations into their surroundings and formation of voids or a material with lower density in the center of segregation channels due to Kirkendall effect.

Název v anglickém jazyce

3D analysis of macrosegregation in twin-roll cast AA3003 alloy before and after heat treatment

Popis výsledku anglicky

Twin-roll casting allows production of sheets and strips with required thickness without subsequent homogenization or hot rolling and therefore has a high potential for industrial applications. One of the drawbacks of this method is a formation of inhomogeneous structure with central segregation. Sheet prepared from 3003 aluminum alloy with 1 wt.% Mn, 0.2 wt.% Fe, 0.5 wt.% Si, 0.2 wt.% Cu and small addition of Zr (0.2 wt.%) and Cr (0.1 wt.%) was studied by X-ray computed tomography. Segregations in the material form as manganese, iron and silicon rich channels spread in the rolling direction. The material annealed at 450 °C exhibits diffusion of alloying elements from segregations into their surroundings and formation of voids or a material with lower density in the center of segregation channels due to Kirkendall effect.

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

—

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2018

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2018 - 27th International Conference on Metallurgy and Materials, Conference Proceedings

ISBN

978-808729484-0

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

1351-1357

Název nakladatele

Tanger, Ltd.

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

23. 5. 2018

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

000461832200217