Characterization of the microstructure of cement paste exposed to gamma radiation by scanning electron microscopy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F25%3AN0000057" target="_blank" >RIV/26722445:_____/25:N0000057 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68407700:21110/25:00386837

Výsledek na webu

<a href="https://ojs.cvut.cz/ojs/index.php/APP/article/view/11100" target="_blank" >https://ojs.cvut.cz/ojs/index.php/APP/article/view/11100</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.14311/APP.2025.54.0072" target="_blank" >10.14311/APP.2025.54.0072</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Characterization of the microstructure of cement paste exposed to gamma radiation by scanning electron microscopy

Popis výsledku v původním jazyce

Hardened cement paste with a water-cement ratio of 0.4 was examined under five different relative humidity (RH) conditions (11 %, 33 %, 76 %, 96 %, and 100 %). These samples were exposed to gamma radiation with a total dose of 13.82 MGy over 341 days. Scanning electron microscopy (SEM) was the primary tool used for characterizing the samples’ microstructure at a microscale, aided by image analysis (IA), which showed negligible changes in Calcium-Silicate-Hydrate phases but a decrease in Portlandite of 1.5–3.5 % under 33–100 % RH conditions. Point elemental analysis was conducted to determine the (Ca-S)/Si ratio of the inner product, finding a significant increase of up to 20 % at medium RH conditions (33–76 %).

Název v anglickém jazyce

Characterization of the microstructure of cement paste exposed to gamma radiation by scanning electron microscopy

Popis výsledku anglicky

Hardened cement paste with a water-cement ratio of 0.4 was examined under five different relative humidity (RH) conditions (11 %, 33 %, 76 %, 96 %, and 100 %). These samples were exposed to gamma radiation with a total dose of 13.82 MGy over 341 days. Scanning electron microscopy (SEM) was the primary tool used for characterizing the samples’ microstructure at a microscale, aided by image analysis (IA), which showed negligible changes in Calcium-Silicate-Hydrate phases but a decrease in Portlandite of 1.5–3.5 % under 33–100 % RH conditions. Point elemental analysis was conducted to determine the (Ca-S)/Si ratio of the inner product, finding a significant increase of up to 20 % at medium RH conditions (33–76 %).

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/GA23-05435S" target="_blank" >GA23-05435S: Účinky radiačního působení na nanomechanické vlastnosti cementových kompozitů v proměnných podmínkách prostředí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Acta Polytechnica CTU Proceedings, vol. 54

ISBN

978-800107507-4

ISSN

—

e-ISSN

—

Počet stran výsledku

7

Strana od-do

72-78

Název nakladatele

—

Místo vydání

—

Místo konání akce

Praha

Datum konání akce

12. 9. 2024

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—