Micromechanical characterization of γ-irradiated cement paste exposed to different relative humidity conditions

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21110%2F24%3A00381433" target="_blank" >RIV/68407700:21110/24:00381433 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/26722445:_____/25:N0000070

Výsledek na webu

<a href="https://doi.org/10.14311/APP.2024.50.0069" target="_blank" >https://doi.org/10.14311/APP.2024.50.0069</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.14311/APP.2024.50.0069" target="_blank" >10.14311/APP.2024.50.0069</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Micromechanical characterization of γ-irradiated cement paste exposed to different relative humidity conditions

Popis výsledku v původním jazyce

In this study, well-hydrated cement paste samples made from Portland cement CEM I-42.5R were gamma irradiated with a 200 TBq 60Co source, resulting in a total absorbed dose of 13.82MGy. During irradiation, the samples were stored under specific relative humidity (RH) conditions of 11 %, 33 %, 76 %, 96 %, and water. Grid nanoindentation was performed on polished sample surfaces to assess the nanoindentation Young’s modulus of both irradiated and non-irradiated control samples. An increase in Young’s modulus by 9.3 % was observed for irradiated samples at low RH (11 %). Samples stored at medium RHs (33 %, 76 %) showed negligible differences in micromechanical properties. However, a significant decrease in Young’s modulus, approximately 15 %, was measured for samples stored at high RHs (96 %, water).

Název v anglickém jazyce

Micromechanical characterization of γ-irradiated cement paste exposed to different relative humidity conditions

Popis výsledku anglicky

In this study, well-hydrated cement paste samples made from Portland cement CEM I-42.5R were gamma irradiated with a 200 TBq 60Co source, resulting in a total absorbed dose of 13.82MGy. During irradiation, the samples were stored under specific relative humidity (RH) conditions of 11 %, 33 %, 76 %, 96 %, and water. Grid nanoindentation was performed on polished sample surfaces to assess the nanoindentation Young’s modulus of both irradiated and non-irradiated control samples. An increase in Young’s modulus by 9.3 % was observed for irradiated samples at low RH (11 %). Samples stored at medium RHs (33 %, 76 %) showed negligible differences in micromechanical properties. However, a significant decrease in Young’s modulus, approximately 15 %, was measured for samples stored at high RHs (96 %, water).

Druh

D - Stať ve sborníku

CEP obor

—

OECD FORD obor

20101 - Civil engineering

Projekt

<a href="/cs/project/GA23-05435S" target="_blank" >GA23-05435S: Účinky radiačního působení na nanomechanické vlastnosti cementových kompozitů v proměnných podmínkách prostředí</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2024

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Local Mechanical Properties 2024

ISBN

978-80-01-07386-5

ISSN

—

e-ISSN

—

Počet stran výsledku

5

Strana od-do

69-73

Název nakladatele

ACTA Polytechnica CTU

Místo vydání

Prague

Místo konání akce

Praha

Datum konání akce

29. 5. 2024

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—