Mitigating environmental assisted cracking in heterogeneous welds by laser peening without coating

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F26722445%3A_____%2F25%3AN0000074" target="_blank" >RIV/26722445:_____/25:N0000074 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/68378271:_____/25:00601810

Výsledek na webu

<a href="https://www.sciencedirect.com/science/article/pii/S1350630724010288" target="_blank" >https://www.sciencedirect.com/science/article/pii/S1350630724010288</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.engfailanal.2024.108982" target="_blank" >10.1016/j.engfailanal.2024.108982</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Mitigating environmental assisted cracking in heterogeneous welds by laser peening without coating

Popis výsledku v původním jazyce

In this work Laser Peening without Coating (LPwC) was applied underwater on heterogeneous weld joint made of P265GH and X6CrNiTi18-10 steel tubes to prevent Environmental Assisted Cracking on the weld/P265GH steel fusion boundary. Special laser head was designed to precisely deliver 200 mJ green laser beam on the centrally located weld interface on the inner surface of a pipe 76 mm wide and 420 mm long. Residual stress analysis revealed that the LPwC treatment led to generation of compressive residual stresses in the critical fusion boundary area with the magnitude of −168 MPa despite the absence of a protective layer in the peening process. The depth of compressive stresses reached up to 0.8 mm. Plastic deformation induced by LPwC led to grain refinement in the microstructure and improved hardness by 16 %. Samples sectioned from the treated pipe were subjected to accelerated corrosion-mechanical testing which showed more than 2.5x increase in cycles to failure after LPwC. Fractography analysis showed shorter length and decreased number of corrosion cracks after LPwC as well as formation of protective oxide layer on top of the treated surface. 3-point bend testing further showed more than 8x increase in corrosion fatigue life.

Název v anglickém jazyce

Mitigating environmental assisted cracking in heterogeneous welds by laser peening without coating

Popis výsledku anglicky

In this work Laser Peening without Coating (LPwC) was applied underwater on heterogeneous weld joint made of P265GH and X6CrNiTi18-10 steel tubes to prevent Environmental Assisted Cracking on the weld/P265GH steel fusion boundary. Special laser head was designed to precisely deliver 200 mJ green laser beam on the centrally located weld interface on the inner surface of a pipe 76 mm wide and 420 mm long. Residual stress analysis revealed that the LPwC treatment led to generation of compressive residual stresses in the critical fusion boundary area with the magnitude of −168 MPa despite the absence of a protective layer in the peening process. The depth of compressive stresses reached up to 0.8 mm. Plastic deformation induced by LPwC led to grain refinement in the microstructure and improved hardness by 16 %. Samples sectioned from the treated pipe were subjected to accelerated corrosion-mechanical testing which showed more than 2.5x increase in cycles to failure after LPwC. Fractography analysis showed shorter length and decreased number of corrosion cracks after LPwC as well as formation of protective oxide layer on top of the treated surface. 3-point bend testing further showed more than 8x increase in corrosion fatigue life.

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

20501 - Materials engineering

Projekt

<a href="/cs/project/EH22_008%2F0004573" target="_blank" >EH22_008/0004573: Průlomové laserové technologie pro chytrou výrobu, vesmírné a biotechnologické aplikace</a><br>

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2025

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Engineering Failure Analysis

ISSN

1350-6307

e-ISSN

1873-1961

Svazek periodika

167A

Číslo periodika v rámci svazku

January

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

15

Strana od-do

1-15

Kód UT WoS článku

001340058300001

EID výsledku v databázi Scopus

2-s2.0-85206831241