The effect of laser shock peening with and without protective coating on intergranular corrosion of sensitized AA5083

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68378271%3A_____%2F22%3A00553424" target="_blank" >RIV/68378271:_____/22:00553424 - isvavai.cz</a>

Nalezeny alternativní kódy

RIV/00216208:11320/22:10446711 RIV/68407700:21340/22:00352556

Výsledek na webu

<a href="https://hdl.handle.net/11104/0339438" target="_blank" >https://hdl.handle.net/11104/0339438</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.1016/j.corsci.2021.109925" target="_blank" >10.1016/j.corsci.2021.109925</a>

Jazyk výsledku

angličtina

Název v původním jazyce

The effect of laser shock peening with and without protective coating on intergranular corrosion of sensitized AA5083

Popis výsledku v původním jazyce

Laser Shock Peening with (LSP) and without protective coating (LPwC) was applied to sensitized AA5083 followed by electrochemical analysis. Potentiodynamic tests indicated a region of increased passivity for the LPwC samples with lower corrosion current. Similarly, significantly reduced intergranular corrosion rate was observed during potentiostatic polarization after LPwC treatment while LSP samples showed only a negligible improvement. The results are attributed to the unique recast surface layer composed of a modified oxide film followed by an embedded oxygen-rich aluminum nanoparticles sub-surface layer without grain boundary β-phase created during laser pulse interaction with the surface when no coating was applied.n

Název v anglickém jazyce

The effect of laser shock peening with and without protective coating on intergranular corrosion of sensitized AA5083

Popis výsledku anglicky

Laser Shock Peening with (LSP) and without protective coating (LPwC) was applied to sensitized AA5083 followed by electrochemical analysis. Potentiodynamic tests indicated a region of increased passivity for the LPwC samples with lower corrosion current. Similarly, significantly reduced intergranular corrosion rate was observed during potentiostatic polarization after LPwC treatment while LSP samples showed only a negligible improvement. The results are attributed to the unique recast surface layer composed of a modified oxide film followed by an embedded oxygen-rich aluminum nanoparticles sub-surface layer without grain boundary β-phase created during laser pulse interaction with the surface when no coating was applied.n

Druh

J_imp - Článek v periodiku v databázi Web of Science

CEP obor

—

OECD FORD obor

10306 - Optics (including laser optics and quantum optics)

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2022

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Corrosion Science

ISSN

0010-938X

e-ISSN

1879-0496

Svazek periodika

194

Číslo periodika v rámci svazku

Jan.

Stát vydavatele periodika

GB - Spojené království Velké Británie a Severního Irska

Počet stran výsledku

13

Strana od-do

109925

Kód UT WoS článku

000720844700002

EID výsledku v databázi Scopus

2-s2.0-85118534065