Analysis of the parameters which influence diffusion processes in the course of homogeneous annealing of AlCu4MgMn alloy
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F13%3A43885608" target="_blank" >RIV/44555601:13420/13:43885608 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Analysis of the parameters which influence diffusion processes in the course of homogeneous annealing of AlCu4MgMn alloy
Popis výsledku v původním jazyce
Homogenization is defined as a method of heat treatment, which consists of holding time at high tempera-ture near the liquidus (approx. 0.7 to 0.8 the melting temperature) to eliminate chemical inhomogeneity diffusion processes. Cause of segregation is selective crystal solidification in the gradual change in compo-sition of the solid phase. Melt began to appear after certain of the hypothermia during cooling, and the growth of germs in accordance with the general laws of crystallization. Each rigid layer has a different chemical composition. The first part of the solid phase ingredient low concentration of the element last, on the contrary, very high. Susceptibility to crystal alloy segregation is greater, the greater the temperature interval solidification of alloys and the horizontal distance between the liquidus and solidus lines. Crystal segregation will also increase with increasing content of alloying elements, which in these experimental alloys occurs as containing 6-9% alloyin
Název v anglickém jazyce
Analysis of the parameters which influence diffusion processes in the course of homogeneous annealing of AlCu4MgMn alloy
Popis výsledku anglicky
Homogenization is defined as a method of heat treatment, which consists of holding time at high tempera-ture near the liquidus (approx. 0.7 to 0.8 the melting temperature) to eliminate chemical inhomogeneity diffusion processes. Cause of segregation is selective crystal solidification in the gradual change in compo-sition of the solid phase. Melt began to appear after certain of the hypothermia during cooling, and the growth of germs in accordance with the general laws of crystallization. Each rigid layer has a different chemical composition. The first part of the solid phase ingredient low concentration of the element last, on the contrary, very high. Susceptibility to crystal alloy segregation is greater, the greater the temperature interval solidification of alloys and the horizontal distance between the liquidus and solidus lines. Crystal segregation will also increase with increasing content of alloying elements, which in these experimental alloys occurs as containing 6-9% alloyin
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JG - Hutnictví, kovové materiály
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2013
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Les problemes contemporains du technosphere et de la formation des cadres d'ingénieurs
ISBN
—
ISSN
2079-2530
e-ISSN
—
Počet stran výsledku
8
Strana od-do
58-65
Název nakladatele
Technopolis
Místo vydání
Donetsk
Místo konání akce
Sevastopol, Ukraine
Datum konání akce
15. 9. 2013
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—