Rating Homogenizing Annealing of the Alloy AlCu4MgMn Image Analysis and EDX Analysis
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F14%3A43886216" target="_blank" >RIV/44555601:13420/14:43886216 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Rating Homogenizing Annealing of the Alloy AlCu4MgMn Image Analysis and EDX Analysis
Popis výsledku v původním jazyce
Homogenization is defined as a method of heat treatment, which consists of holding time at high temperature near the liquidus (approx. 0.7 to 0.8 the melting temperature) to eliminate chemical inhomogeneity diffusion processes. Cause of segregation is selective crystal solidification in the gradual change in composition of the solid phase. Melt began to appear after certain of the hypothermia during cooling, and the growth of germs in accordance with the general laws of crystallization. Each rigid layerhas a different chemical composition. The first part of the solid phase ingredient low concentration of the element last, on the contrary, very high. Susceptibility to crystal alloy segregation is greater, the greater the temperature interval solidification of alloys and the horizontal distance between the liquidus and solidus lines. Crystal segregation will also increase with increasing content of alloying elements, which in these experimental alloys occurs as containing 6-9% alloying
Název v anglickém jazyce
Rating Homogenizing Annealing of the Alloy AlCu4MgMn Image Analysis and EDX Analysis
Popis výsledku anglicky
Homogenization is defined as a method of heat treatment, which consists of holding time at high temperature near the liquidus (approx. 0.7 to 0.8 the melting temperature) to eliminate chemical inhomogeneity diffusion processes. Cause of segregation is selective crystal solidification in the gradual change in composition of the solid phase. Melt began to appear after certain of the hypothermia during cooling, and the growth of germs in accordance with the general laws of crystallization. Each rigid layerhas a different chemical composition. The first part of the solid phase ingredient low concentration of the element last, on the contrary, very high. Susceptibility to crystal alloy segregation is greater, the greater the temperature interval solidification of alloys and the horizontal distance between the liquidus and solidus lines. Crystal segregation will also increase with increasing content of alloying elements, which in these experimental alloys occurs as containing 6-9% alloying
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JR - Ostatní strojírenství
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
V - Vyzkumna aktivita podporovana z jinych verejnych zdroju
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
KOm-CAST
ISBN
978-83-63666-90-3
ISSN
—
e-ISSN
—
Počet stran výsledku
6
Strana od-do
77-82
Název nakladatele
RSdruk, Polsko
Místo vydání
Swilcza
Místo konání akce
Swilcza, Polsko
Datum konání akce
9. 9. 2014
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—