Complex analysis of the quality of the nickel layer of screws.
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F16%3A43888077" target="_blank" >RIV/44555601:13420/16:43888077 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Complex analysis of the quality of the nickel layer of screws.
Popis výsledku v původním jazyce
Chemical nickel plating is one of the functional coatings that extend the life of coated components. This type of coating has wide application, enables coated complex shape components, holes and edges. The procedure electro less nickel has several steps and consists of degreasing, rinsing, pickling (eg. Hydrochloric acid), rinsing, and insert into the nickel bath. Nickel coatings do not form pure nickel, but it is a phase of NiP, NiB, NiCoP, etc. The thickness and quality of the layer depends on the purity of the object, and the time of stamina the concentration in the bath. Follow by removal from the bath, rinsing and drying. The coating has a hardness of about 550 HV, given that it is an alloy coating nickel-phosphorus can be achieved by heat treatment hardness of 1000 HV. Chemical nickel coating is universal coating that their properties coated component simultaneously provides corrosion resistance, abrasion resistance and good sliding properties. The coatings exhibit a constant thickness across the plating surface, regardless of its geometry. In most common applications are used in coating thickness 25 ?m, a thickness of 25 to 80 ?m are used for the parts with a higher the risks to corrosion and the thickness of 80 ?m for the repair of wear parts and the like. The aim of the paper was to analyse the quality of the nickel layer of screws of free-cutting steel, which are part of the fuel system of cars. Nickel coating of steel parts is carried out with the aim of extending the life of components. Any degradation of the layer results in deterioration of not only of screws, but also the whole. Layers will be evaluated using a microscopic methods and hardness measurements. The results will determine the causes of changes in the quality of the nickel layer and a determined of general and specific recommendations for the formation of the nickel layer.
Název v anglickém jazyce
Complex analysis of the quality of the nickel layer of screws.
Popis výsledku anglicky
Chemical nickel plating is one of the functional coatings that extend the life of coated components. This type of coating has wide application, enables coated complex shape components, holes and edges. The procedure electro less nickel has several steps and consists of degreasing, rinsing, pickling (eg. Hydrochloric acid), rinsing, and insert into the nickel bath. Nickel coatings do not form pure nickel, but it is a phase of NiP, NiB, NiCoP, etc. The thickness and quality of the layer depends on the purity of the object, and the time of stamina the concentration in the bath. Follow by removal from the bath, rinsing and drying. The coating has a hardness of about 550 HV, given that it is an alloy coating nickel-phosphorus can be achieved by heat treatment hardness of 1000 HV. Chemical nickel coating is universal coating that their properties coated component simultaneously provides corrosion resistance, abrasion resistance and good sliding properties. The coatings exhibit a constant thickness across the plating surface, regardless of its geometry. In most common applications are used in coating thickness 25 ?m, a thickness of 25 to 80 ?m are used for the parts with a higher the risks to corrosion and the thickness of 80 ?m for the repair of wear parts and the like. The aim of the paper was to analyse the quality of the nickel layer of screws of free-cutting steel, which are part of the fuel system of cars. Nickel coating of steel parts is carried out with the aim of extending the life of components. Any degradation of the layer results in deterioration of not only of screws, but also the whole. Layers will be evaluated using a microscopic methods and hardness measurements. The results will determine the causes of changes in the quality of the nickel layer and a determined of general and specific recommendations for the formation of the nickel layer.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
—
Návaznosti
S - Specificky vyzkum na vysokych skolach
Ostatní
Rok uplatnění
2016
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Engineering for Rural Development, Proceedings
ISBN
—
ISSN
1691-5976
e-ISSN
—
Počet stran výsledku
6
Strana od-do
1212-1217
Název nakladatele
Latvia University of Agriculture Faculty of Engineering
Místo vydání
Jelgava, Latvia
Místo konání akce
Jelgava
Datum konání akce
25. 5. 2016
Typ akce podle státní příslušnosti
EUR - Evropská akce
Kód UT WoS článku
—