Structural Aspects of Decreasing the Corrosion Resistance of Zinc Coating Obtained in Baths with Al, Ni, and Pb Additives
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F20%3A00345293" target="_blank" >RIV/68407700:21220/20:00345293 - isvavai.cz</a>
Výsledek na webu
<a href="https://doi.org/10.3390/ma13020385" target="_blank" >https://doi.org/10.3390/ma13020385</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.3390/ma13020385" target="_blank" >10.3390/ma13020385</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Structural Aspects of Decreasing the Corrosion Resistance of Zinc Coating Obtained in Baths with Al, Ni, and Pb Additives
Popis výsledku v původním jazyce
The article presented the results of tests determining the synergistic effect of Al, Ni, and Pb additions on a zinc bath on the structure and corrosion resistance of coatings obtained on low silicon steel. Analyzed coatings were produced on S235JRG2 steel with Si content of 0.02 mass%. The corrosion resistance of the coatings was compared with the corrosion resistance of the coating obtained in the "pure" zinc bath. Structure at high magnifications (SEM) was determined, as well as coating thickness and chemical composition in microspheres. The corrosion resistance of the coatings was established comparatively in standard corrosion tests in neutral salt spray and a humid atmosphere containing SO2. It was found that the addition of Pb to the zinc bath reduced the corrosion resistance of the coatings. In the coating structure obtained in the Zn-AlNiPb bath, lead precipitation was observed in both the outer layer and the intermediate layer of the coating. Grain boundaries were the preferred site for lead precipitation. The presence of Pb precipitates favored conditions for the creation of additional corrosion cells, which led to a decrease in the corrosion resistance of the coatings.
Název v anglickém jazyce
Structural Aspects of Decreasing the Corrosion Resistance of Zinc Coating Obtained in Baths with Al, Ni, and Pb Additives
Popis výsledku anglicky
The article presented the results of tests determining the synergistic effect of Al, Ni, and Pb additions on a zinc bath on the structure and corrosion resistance of coatings obtained on low silicon steel. Analyzed coatings were produced on S235JRG2 steel with Si content of 0.02 mass%. The corrosion resistance of the coatings was compared with the corrosion resistance of the coating obtained in the "pure" zinc bath. Structure at high magnifications (SEM) was determined, as well as coating thickness and chemical composition in microspheres. The corrosion resistance of the coatings was established comparatively in standard corrosion tests in neutral salt spray and a humid atmosphere containing SO2. It was found that the addition of Pb to the zinc bath reduced the corrosion resistance of the coatings. In the coating structure obtained in the Zn-AlNiPb bath, lead precipitation was observed in both the outer layer and the intermediate layer of the coating. Grain boundaries were the preferred site for lead precipitation. The presence of Pb precipitates favored conditions for the creation of additional corrosion cells, which led to a decrease in the corrosion resistance of the coatings.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20506 - Coating and films
Návaznosti výsledku
Projekt
—
Návaznosti
N - Vyzkumna aktivita podporovana z neverejnych zdroju
Ostatní
Rok uplatnění
2020
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Materials
ISSN
1996-1944
e-ISSN
1996-1944
Svazek periodika
13
Číslo periodika v rámci svazku
2
Stát vydavatele periodika
CH - Švýcarská konfederace
Počet stran výsledku
14
Strana od-do
—
Kód UT WoS článku
000515499900132
EID výsledku v databázi Scopus
2-s2.0-85081087358