Geopolymer suspension containing nanoparticles for heat-resistant coatings and method of the production thereof

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F44555601%3A13420%2F23%3A43898192" target="_blank" >RIV/44555601:13420/23:43898192 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Geopolymer suspension containing nanoparticles for heat-resistant coatings and method of the production thereof

Popis výsledku v původním jazyce

The invention relates to a geopolymer suspension for insoluble heat- and corrosion-resistant coatings on the surfaces of Fe alloy products, which contains 20 to 25 mass%. aqueous solution of 80 to 90 percent phosphoric acid, 25 to 30 wt.% aluminosilicate, 4.6 to 5.2 wt.% graphite and the remainder isopropyl alcohol. It also refers to the method of preparing a geopolymer suspension, in which an aqueous solution of 80 to 90 percent phosphoric acid is added to 100 ml of isopropyl alcohol and stirred at laboratory temperature for 8 to 15 min. Aluminosilicate is gradually added, and after 9 to 15 min. while stirring, graphite is added once as an additive and the resulting mixture is homogenized for another 18 to 25 min.

Název v anglickém jazyce

Geopolymer suspension containing nanoparticles for heat-resistant coatings and method of the production thereof

Popis výsledku anglicky

The invention relates to a geopolymer suspension for insoluble heat- and corrosion-resistant coatings on the surfaces of Fe alloy products, which contains 20 to 25 mass%. aqueous solution of 80 to 90 percent phosphoric acid, 25 to 30 wt.% aluminosilicate, 4.6 to 5.2 wt.% graphite and the remainder isopropyl alcohol. It also refers to the method of preparing a geopolymer suspension, in which an aqueous solution of 80 to 90 percent phosphoric acid is added to 100 ml of isopropyl alcohol and stirred at laboratory temperature for 8 to 15 min. Aluminosilicate is gradually added, and after 9 to 15 min. while stirring, graphite is added once as an additive and the resulting mixture is homogenized for another 18 to 25 min.

Druh

P - Patent

CEP obor

—

OECD FORD obor

21001 - Nano-materials (production and properties)

Projekt

<a href="/cs/project/EF18_069%2F0010045" target="_blank" >EF18_069/0010045: Vývoj nových nano a mikro povlaků na povrchu vybraných kovových materiálů - NANOTECH ITI II</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2023

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Číslo patentu nebo vzoru

GB 2619150

Vydavatel

ES001 -

Název vydavatele

Spanish Patent and Trademark Office

Místo vydání

Madrid

Stát vydání

ES - Španělské království

Datum přijetí

27. 3. 2023

Název vlastníka

Univerzita jana Evangelisty Purkyně

Způsob využití

B - Výsledek je využíván orgány státní nebo veřejné správy

Druh možnosti využití

A - K využití výsledku jiným subjektem je vždy nutné nabytí licence