Corrosion behavior of steels in flowing lead?bismuth under abnormal conditions

Popis výsledku v původním jazyce

The project IP EUROTRANS, domain DEMETRA, is primary focused on the study of the technology of the interaction between steels and heavy liquid metals. The characterization of the metal response to sudden changes, simulating accidental conditions in liquid lead?bismuth eutectic was carried out. This paper reports the results of two hot-spot simulations with two different oxygen concentrations. Each experiment was divided in two main periods: the initial, long period at the standard operating temperature550 °C; the second, short period, at higher temperature, 650 °C. The damage that occurs on the austenitic steel AISI 316L and the ferritic?martensitic steel T91 was investigated.

Název v anglickém jazyce

Corrosion behavior of steels in flowing lead?bismuth under abnormal conditions

Popis výsledku anglicky

The project IP EUROTRANS, domain DEMETRA, is primary focused on the study of the technology of the interaction between steels and heavy liquid metals. The characterization of the metal response to sudden changes, simulating accidental conditions in liquid lead?bismuth eutectic was carried out. This paper reports the results of two hot-spot simulations with two different oxygen concentrations. Each experiment was divided in two main periods: the initial, long period at the standard operating temperature550 °C; the second, short period, at higher temperature, 650 °C. The damage that occurs on the austenitic steel AISI 316L and the ferritic?martensitic steel T91 was investigated.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/GA106%2F07%2F1145" target="_blank" >GA106/07/1145: Degradace konstrukčních ocelí v těžkých tekutých kovech</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2008

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Journal of Nuclear Materials

ISSN

0022-3115

e-ISSN

—

Svazek periodika

376

Číslo periodika v rámci svazku

3

Stát vydavatele periodika

NL - Nizozemsko

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—