Loading of working surfaces of cams – contact pressure

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46709002%3A_____%2F18%3AN0000065" target="_blank" >RIV/46709002:_____/18:N0000065 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Loading of working surfaces of cams – contact pressure
Popis výsledku v původním jazyce
"During cam mechanism operation the fatigue damage of the contact surfaces of the cam and the roller can occur. This damage can be in the form of pittings or micropittings or the abrasion may occur, and at the surface-coated cams the surface layer may peel. The pitting is a surface fatigue damage of the material due to long-term cyclic stress loading above the fatigue life of the material. The pits about 1 mm occur, which result from spreading the subsurface cracks, or the larger surface portions of the material can peel."
Název v anglickém jazyce
Loading of working surfaces of cams – contact pressure
Popis výsledku anglicky
"During cam mechanism operation the fatigue damage of the contact surfaces of the cam and the roller can occur. This damage can be in the form of pittings or micropittings or the abrasion may occur, and at the surface-coated cams the surface layer may peel. The pitting is a surface fatigue damage of the material due to long-term cyclic stress loading above the fatigue life of the material. The pits about 1 mm occur, which result from spreading the subsurface cracks, or the larger surface portions of the material can peel."

Projekt
<a href="/cs/project/LO1213" target="_blank" >LO1213: Excelentní Strojírenský Výzkum</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění
2018
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)