Assessment of the structure and high temperature strength of Fe-35Al-5Zr intermetallic alloy

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24210%2F13%3A%230005679" target="_blank" >RIV/46747885:24210/13:#0005679 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.metal2013.com/files/proceedings/12/reports/1425.pdf" target="_blank" >http://www.metal2013.com/files/proceedings/12/reports/1425.pdf</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Assessment of the structure and high temperature strength of Fe-35Al-5Zr intermetallic alloy

Popis výsledku v původním jazyce

Exceptional high-temperature oxidation resistance makes iron aluminides promising candidates to replace Ni-Cr-based stainless steels. On the other hand these alloys suffer from insufficient high-temperature strength. Addition of Zr leads to formation ofhard intermetallic phases that increase a high-temperature strength. Correlative microscopy has been used for investigation of the structure in both as cast and annealed state, the high-temperature mechanical strength has been measured in a temperature range from 600 to 950°C. It has been shown that formation of Zr-containing (Fe,Al)12Zr ?1-phase and (Fe,Al)2Zr Laves phase leads to a significant gain in ?0.2 yield stress; however BTDT shifts to higher temperatures.

Název v anglickém jazyce

Assessment of the structure and high temperature strength of Fe-35Al-5Zr intermetallic alloy

Popis výsledku anglicky

Exceptional high-temperature oxidation resistance makes iron aluminides promising candidates to replace Ni-Cr-based stainless steels. On the other hand these alloys suffer from insufficient high-temperature strength. Addition of Zr leads to formation ofhard intermetallic phases that increase a high-temperature strength. Correlative microscopy has been used for investigation of the structure in both as cast and annealed state, the high-temperature mechanical strength has been measured in a temperature range from 600 to 950°C. It has been shown that formation of Zr-containing (Fe,Al)12Zr ?1-phase and (Fe,Al)2Zr Laves phase leads to a significant gain in ?0.2 yield stress; however BTDT shifts to higher temperatures.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/GAP108%2F12%2F1452" target="_blank" >GAP108/12/1452: Optimalizace vysokoteplotních mechanických vlastností aluminidů železa typu Fe3Al s karbidotvornými prvky</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2013

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

METAL 2013 - Proceedings of 22nd International Conference on Metallurgy and Materials

ISBN

978-80-87294-41-3

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

1491-1498

Název nakladatele

Tanger, s.r.o.

Místo vydání

Ostrava

Místo konání akce

Brno

Datum konání akce

1. 1. 2013

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—