Tribology of Titanium-Aluminium Base Nanomultilayer Coatings

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F46747885%3A24620%2F16%3A00000435" target="_blank" >RIV/46747885:24620/16:00000435 - isvavai.cz</a>

Výsledek na webu

<a href="http://mnmt.fvtm.ujep.cz/" target="_blank" >http://mnmt.fvtm.ujep.cz/</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Tribology of Titanium-Aluminium Base Nanomultilayer Coatings

Popis výsledku v původním jazyce

The article presents investigation of the trybological properties, particularly dry friction and friction using a process fluid, of friction pairs of steel ball against titanium-aluminium base nanomultilayer (NML) coatings. The coatings are deposited by cathodic arc evaporation of both pure titanium and aluminium with eighteen per-cent silicon cathodes. Each multilayer structure consists of 49 bi-layers. The external deposited layeris with five times longer growing period. The coatings are deposited at the temperature of 400°C and the work pressure of 2 Pa. Polished steel discs (Ø 20 mm × 5 mm thick) are used as the substrate material. The measured dry friction coeficients are in the range of 0.216 – 0.356 and the coefficients friction using process fluid is in the range of 0.085 – 0.151. The calculated wear of the counter-body is in the range of (0.66÷ 4.21)x10-3 mm3, asit depends on the friction conditions and the used multilayer coating.

Název v anglickém jazyce

Tribology of Titanium-Aluminium Base Nanomultilayer Coatings

Popis výsledku anglicky

The article presents investigation of the trybological properties, particularly dry friction and friction using a process fluid, of friction pairs of steel ball against titanium-aluminium base nanomultilayer (NML) coatings. The coatings are deposited by cathodic arc evaporation of both pure titanium and aluminium with eighteen per-cent silicon cathodes. Each multilayer structure consists of 49 bi-layers. The external deposited layeris with five times longer growing period. The coatings are deposited at the temperature of 400°C and the work pressure of 2 Pa. Polished steel discs (Ø 20 mm × 5 mm thick) are used as the substrate material. The measured dry friction coeficients are in the range of 0.216 – 0.356 and the coefficients friction using process fluid is in the range of 0.085 – 0.151. The calculated wear of the counter-body is in the range of (0.66÷ 4.21)x10-3 mm3, asit depends on the friction conditions and the used multilayer coating.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JK - Koroze a povrchové úpravy materiálu

OECD FORD obor

—

Projekt

<a href="/cs/project/LO1201" target="_blank" >LO1201: ROZVOJ ÚSTAVU PRO NANOMATERIÁLY, POKROČILÉ TECHNOLOGIE A INOVACE TECHNICKÉ UNIVERZITY V LIBERCI</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2016

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Manufacturing technology

ISSN

1213-2489

e-ISSN

—

Svazek periodika

16

Číslo periodika v rámci svazku

5

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

6

Strana od-do

859-864

Kód UT WoS článku

—

EID výsledku v databázi Scopus

2-s2.0-84997080079