Microstructural stability of 10Cr1MoW steel during long-term creep testing

Popis výsledku v původním jazyce

Material of trial rotor made of m,artensitic X12CrMoWVNbN10-1-1 steel underwent creep testing to the rupture in the temperature range from 500 °C to 600 °C. Microstructures of selected specimens tested at 500 °C and 575 °C that ruptured after exposures exceeding 100,000 hrs and 60,000 hrs, respectively, were studied in detail using light, scanning and transmission electron microscopy. Quantitative analysis of substructure was carried out. Tempered martensite consisted of ferritic laths with subgrains, coarse particles at grain and subgrain boundaries and fine intragranular precipitate. A significant increase in size of subgrains and a slight growth of coarse particles of secondary phases were found out after the test at conditions 500 °C/250 MPa/107,514 hrs, while volume fraction of particles was almost the same as in virgin material. Time to rupture was almost twice longer than it was predicted. Influence of microstructural changes on the creep strength is discussed.

Název v anglickém jazyce

Microstructural stability of 10Cr1MoW steel during long-term creep testing

Popis výsledku anglicky

Material of trial rotor made of m,artensitic X12CrMoWVNbN10-1-1 steel underwent creep testing to the rupture in the temperature range from 500 °C to 600 °C. Microstructures of selected specimens tested at 500 °C and 575 °C that ruptured after exposures exceeding 100,000 hrs and 60,000 hrs, respectively, were studied in detail using light, scanning and transmission electron microscopy. Quantitative analysis of substructure was carried out. Tempered martensite consisted of ferritic laths with subgrains, coarse particles at grain and subgrain boundaries and fine intragranular precipitate. A significant increase in size of subgrains and a slight growth of coarse particles of secondary phases were found out after the test at conditions 500 °C/250 MPa/107,514 hrs, while volume fraction of particles was almost the same as in virgin material. Time to rupture was almost twice longer than it was predicted. Influence of microstructural changes on the creep strength is discussed.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/OC09041" target="_blank" >OC09041: Mikrostrukturní výzkum svarových spojů progresivních žáropevných materiálů pro tepelné elektrárny</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

18. Mezinárodní metalurgická konference METAL 2009

ISBN

978-80-87294-03-1

ISSN

—

e-ISSN

—

Počet stran výsledku

8

Strana od-do

—

Název nakladatele

Tanger s.r.o.

Místo vydání

Ostrava

Místo konání akce

Hradec nad Moravicí

Datum konání akce

1. 1. 2009

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—