Creep Testing and Microstructure of Weld Joint in the Pipe Made of P92 Steel

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F47718684%3A_____%2F09%3A%230000363" target="_blank" >RIV/47718684:_____/09:#0000363 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Creep Testing and Microstructure of Weld Joint in the Pipe Made of P92 Steel

Popis výsledku v původním jazyce

One-side weld joint of W type was prepared from P92 type steel using GTAW & SMAW method. Creep testing of smooth cross-weld samples at temperatures ranging from 575 to 650 °C and at stresses from 70 to 240 MPa was carried out. Ruptured samples were undergone fractographic analysis and extended metallographic investigation including scanning and transmission electron microscopy. After creep tests at temperatures above 575°C increase in size of secondary phases and cavities formation were evident. Voids were concentrated in fine prior austenite grain heat affected zones, where fracture occurred. In addition, sporadic occurrence of individual cavities was found out in the base material and the weld metal after tests at 625 and 650 °C. During creep exposures at temperatures above 600 °C Laves phase precipitated.

Název v anglickém jazyce

Creep Testing and Microstructure of Weld Joint in the Pipe Made of P92 Steel

Popis výsledku anglicky

One-side weld joint of W type was prepared from P92 type steel using GTAW & SMAW method. Creep testing of smooth cross-weld samples at temperatures ranging from 575 to 650 °C and at stresses from 70 to 240 MPa was carried out. Ruptured samples were undergone fractographic analysis and extended metallographic investigation including scanning and transmission electron microscopy. After creep tests at temperatures above 575°C increase in size of secondary phases and cavities formation were evident. Voids were concentrated in fine prior austenite grain heat affected zones, where fracture occurred. In addition, sporadic occurrence of individual cavities was found out in the base material and the weld metal after tests at 625 and 650 °C. During creep exposures at temperatures above 600 °C Laves phase precipitated.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

<a href="/cs/project/OC09041" target="_blank" >OC09041: Mikrostrukturní výzkum svarových spojů progresivních žáropevných materiálů pro tepelné elektrárny</a><br>

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

2009

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

IIW International Conference on Advances in Welding and Allied Technologies

ISBN

978-981-08-3259-9

ISSN

—

e-ISSN

—

Počet stran výsledku

6

Strana od-do

—

Název nakladatele

Singapore Welding Society

Místo vydání

Songapore

Místo konání akce

Singapore

Datum konání akce

1. 1. 2009

Typ akce podle státní příslušnosti

WRD - Celosvětová akce

Kód UT WoS článku

—