Influence of Annealing Temperature and Time on the Mechanical Properties of Selected Steels for Heavy Forgings

Kód výsledku v IS VaVaI

RIV/47718684:_____/15:#0000599 - isvavai.cz

Výsledek na webu

http://dx.doi.org/10.4028/www.scientific.net/KEM.647.38

DOI - Digital Object Identifier

10.4028/www.scientific.net/KEM.647.38

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Annealing Temperature and Time on the Mechanical Properties of Selected Steels for Heavy Forgings

Popis výsledku v původním jazyce

Two types of steels used for production of heavy forgings were selected for the experimental evaluation. The effect of long time dwell at elevated temperatures and cooling during heat treatment on their mechanical properties was monitored in order to avoid the possibility of grain boundary embrittlement. Samples from evaluated steels 26NiCrMoV14-5 and 22CrNiMoWV8-8 were austenitized for 2 hours at temperature of 1200°C and oil quenched. Subsequently the annealing at temperatures (200 - 700)°C for 1 hourand 100 hours was applied. Selected mechanical properties, especially hardness and impact energy, were monitored. It was found that for steels 26NiCrMoV14-5 and 22CrMoNiWV8-8 exist the temperature intervals (300 - 400)°C and (500 - 600)°C respectively with the possible potential for toughness decreasing.

Název v anglickém jazyce

Influence of Annealing Temperature and Time on the Mechanical Properties of Selected Steels for Heavy Forgings

Popis výsledku anglicky

Two types of steels used for production of heavy forgings were selected for the experimental evaluation. The effect of long time dwell at elevated temperatures and cooling during heat treatment on their mechanical properties was monitored in order to avoid the possibility of grain boundary embrittlement. Samples from evaluated steels 26NiCrMoV14-5 and 22CrNiMoWV8-8 were austenitized for 2 hours at temperature of 1200°C and oil quenched. Subsequently the annealing at temperatures (200 - 700)°C for 1 hourand 100 hours was applied. Selected mechanical properties, especially hardness and impact energy, were monitored. It was found that for steels 26NiCrMoV14-5 and 22CrMoNiWV8-8 exist the temperature intervals (300 - 400)°C and (500 - 600)°C respectively with the possible potential for toughness decreasing.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

FR-TI2/132: Výzkum příčin výrobních vad hmotných výkovků a odlitků s nejvyššími jakostními parametry pro parní, větrné a jaderné elektrárny

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Key engineering materials

ISSN

1662-9795

e-ISSN

—

Svazek periodika

647

Číslo periodika v rámci svazku

2015

Stát vydavatele periodika

CH - Švýcarská konfederace

Počet stran výsledku

9

Strana od-do

38-46

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—