Influence of Annealing Temperature and Time on the Mechanical Properties of Selected Steels for Heavy Forgings

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F15%3A00230650" target="_blank" >RIV/68407700:21220/15:00230650 - isvavai.cz</a>

Výsledek na webu

<a href="http://www.scientific.net/KEM.647.38" target="_blank" >http://www.scientific.net/KEM.647.38</a>

DOI - Digital Object Identifier

<a href="http://dx.doi.org/10.4028/www.scientific.net/KEM.647.38" target="_blank" >10.4028/www.scientific.net/KEM.647.38</a>

Jazyk výsledku

angličtina

Název v původním jazyce

Influence of Annealing Temperature and Time on the Mechanical Properties of Selected Steels for Heavy Forgings

Popis výsledku v původním jazyce

Two types of steels used for production of heavy forgings were selected for the experimental evaluation of the effect of long time dwell at elevated temperatures and cooling during heat treatment on their mechanical properties in order avoid the possibility of grain boundary embrittlement. Samples from evaluated steels 26NiCrMoV14-5 and 22CrNiMoWV8-8 were austenitized for 2 hours at temperature of 1200°C and oil quenched. Subsequently the annealing at temperatures (200 - 700)°C for 1 hour and 100 hours was applied. Selected mechanical properties, especially hardness and impact energy, were monitored. It was found that for steels 26NiCrMoV14-5 and 22CrMoNiWV8-8 exist the temperature intervals (300 - 400)°C and (500 - 600)°C respectively with the possible potential for toughness decreasing.

Název v anglickém jazyce

Influence of Annealing Temperature and Time on the Mechanical Properties of Selected Steels for Heavy Forgings

Popis výsledku anglicky

Two types of steels used for production of heavy forgings were selected for the experimental evaluation of the effect of long time dwell at elevated temperatures and cooling during heat treatment on their mechanical properties in order avoid the possibility of grain boundary embrittlement. Samples from evaluated steels 26NiCrMoV14-5 and 22CrNiMoWV8-8 were austenitized for 2 hours at temperature of 1200°C and oil quenched. Subsequently the annealing at temperatures (200 - 700)°C for 1 hour and 100 hours was applied. Selected mechanical properties, especially hardness and impact energy, were monitored. It was found that for steels 26NiCrMoV14-5 and 22CrMoNiWV8-8 exist the temperature intervals (300 - 400)°C and (500 - 600)°C respectively with the possible potential for toughness decreasing.

Druh

D - Stať ve sborníku

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2015

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Key Engineering Materials (Contribution of Metallography to Solving Production Problems)

ISBN

—

ISSN

1013-9826

e-ISSN

—

Počet stran výsledku

9

Strana od-do

38-46

Název nakladatele

Trans Tech Publications Inc.

Místo vydání

Uetikon-Zurich

Místo konání akce

Lázně Libverda

Datum konání akce

17. 6. 2014

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—