Effects of Heat Treatment on Additively Manufactured 316L Stainless Steel
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23210%2F22%3A43970247" target="_blank" >RIV/49777513:23210/22:43970247 - isvavai.cz</a>
Výsledek na webu
<a href="https://journalmt.com/artkey/mft-202203-0012_effects-of-heat-treatment-on-additively-manufactured-316l-stainless-steel.php" target="_blank" >https://journalmt.com/artkey/mft-202203-0012_effects-of-heat-treatment-on-additively-manufactured-316l-stainless-steel.php</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.21062/mft.2022.042" target="_blank" >10.21062/mft.2022.042</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Effects of Heat Treatment on Additively Manufactured 316L Stainless Steel
Popis výsledku v původním jazyce
The microstructure and mechanical properties of selectively laser melting (SLM)-manufactured 316L stainlesssteele were evaluated by scanning electron microscopy, tensile testing at ambient temperature andCharpy impact test. These samples were compared with as-built samples. Following heat treatment conditionswere used: 500 °C for 2/4 hours, 650 °C for 2 hours and 900 °C for 1 hour. Cooling took place infurnace and in furnace with opened valve. Compared to as built samples the heat treatment at lowertemperature negatively influenced elongation but increased the amount of energy absorbed by materialduring fracture.
Název v anglickém jazyce
Effects of Heat Treatment on Additively Manufactured 316L Stainless Steel
Popis výsledku anglicky
The microstructure and mechanical properties of selectively laser melting (SLM)-manufactured 316L stainlesssteele were evaluated by scanning electron microscopy, tensile testing at ambient temperature andCharpy impact test. These samples were compared with as-built samples. Following heat treatment conditionswere used: 500 °C for 2/4 hours, 650 °C for 2 hours and 900 °C for 1 hour. Cooling took place infurnace and in furnace with opened valve. Compared to as built samples the heat treatment at lowertemperature negatively influenced elongation but increased the amount of energy absorbed by materialduring fracture.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/EF18_069%2F0010040" target="_blank" >EF18_069/0010040: Výzkum aditivních technologií pro budoucí uplatnění ve strojírenské praxi - RTI plus</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2022
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
Manufacturing Technology
ISSN
1213-2489
e-ISSN
2787-9402
Svazek periodika
22
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
CZ - Česká republika
Počet stran výsledku
6
Strana od-do
261-266
Kód UT WoS článku
000859956800001
EID výsledku v databázi Scopus
2-s2.0-85133778692