Structure and properties of hard and superhard Zr-Cu-N nanocomposite coatings

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F00%3A00053565" target="_blank" >RIV/49777513:23520/00:00053565 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Structure and properties of hard and superhard Zr-Cu-N nanocomposite coatings

Popis výsledku v původním jazyce

Zr-Cu-N nanocomposite films represent a new material of the type-nanocrystalline transition metal nitride (nc-MeN)/metal. In the present work, films were deposited onto steel substrates using unbalanced dc reactive magnetron sputtering of a Zr-Cu (62/38at.%) target. Film structure, chemical composition, mechanical and optical properties were investigated by means of X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, wavelengthdispersive electron probe microanalysis, depth-sensing microindentation and spectroscopic ellipsometry. It was found that (i) there is a strong correlation between the film structure, Cu content and film properties and (ii) either hard or superhard Zr-Cu-N films can be formed. The superhard coatings with hardness H > 40 GPa are characterized by a columnar structure, a strong 111 XRD peak from ZrN grains and no diffraction peaks from Cu.

Název v anglickém jazyce

Structure and properties of hard and superhard Zr-Cu-N nanocomposite coatings

Popis výsledku anglicky

Zr-Cu-N nanocomposite films represent a new material of the type-nanocrystalline transition metal nitride (nc-MeN)/metal. In the present work, films were deposited onto steel substrates using unbalanced dc reactive magnetron sputtering of a Zr-Cu (62/38at.%) target. Film structure, chemical composition, mechanical and optical properties were investigated by means of X-ray diffraction (XRD), scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy, wavelengthdispersive electron probe microanalysis, depth-sensing microindentation and spectroscopic ellipsometry. It was found that (i) there is a strong correlation between the film structure, Cu content and film properties and (ii) either hard or superhard Zr-Cu-N films can be formed. The superhard coatings with hardness H > 40 GPa are characterized by a columnar structure, a strong 111 XRD peak from ZrN grains and no diffraction peaks from Cu.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)

Rok uplatnění

2000

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Materials Science and Engineering

ISSN

09215093

e-ISSN

—

Svazek periodika

1

Číslo periodika v rámci svazku

Č. A289

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

9

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—