ZrN/Cu nanocomposite film-anovel superhard material

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23520%2F99%3A00044453" target="_blank" >RIV/49777513:23520/99:00044453 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

ZrN/Cu nanocomposite film-anovel superhard material

Popis výsledku v původním jazyce

This article reports on the structure and hardness of ZrCu-N films prepared by dc reactive magnetron sputtering of a ZrCu alloyed target in a mixture of Ar+N2 using a round planar unbalanced magnetron of diameter 100 mm. It was found that there is a strong correlation between the structure of the film and its hardness. The hard (<40 GPa) ZrCu-N films are characterized by many weak reflections from poly-oriented ZrN and Cu grains. In contrast, the superhard (>=40 GPa) ZrCu-N films are characterized by astrong reflection from ZrN grains with a dominate ZrN(111) orientation and no reflections from Cu. The superhard ZrCu-N films with a hardness of 54 GPa are nc-ZrN/Cu nanocomposite films composed of strongly oriented ZrN grains surrounded by a thin layerof Cu. These films exhibit a high elastic recovery of about 80% (determined by a microhardness tester) and contain approximately 1-2 wt.% Cu. The superhard nc-ZrN/Cu nanocomposite films represent a new class of superhard materials.

Název v anglickém jazyce

ZrN/Cu nanocomposite film-anovel superhard material

Popis výsledku anglicky

This article reports on the structure and hardness of ZrCu-N films prepared by dc reactive magnetron sputtering of a ZrCu alloyed target in a mixture of Ar+N2 using a round planar unbalanced magnetron of diameter 100 mm. It was found that there is a strong correlation between the structure of the film and its hardness. The hard (<40 GPa) ZrCu-N films are characterized by many weak reflections from poly-oriented ZrN and Cu grains. In contrast, the superhard (>=40 GPa) ZrCu-N films are characterized by astrong reflection from ZrN grains with a dominate ZrN(111) orientation and no reflections from Cu. The superhard ZrCu-N films with a hardness of 54 GPa are nc-ZrN/Cu nanocomposite films composed of strongly oriented ZrN grains surrounded by a thin layerof Cu. These films exhibit a high elastic recovery of about 80% (determined by a microhardness tester) and contain approximately 1-2 wt.% Cu. The superhard nc-ZrN/Cu nanocomposite films represent a new class of superhard materials.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

BL - Fyzika plasmatu a výboje v plynech

OECD FORD obor

—

Projekt

Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.

Návaznosti

P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)<br>Z - Vyzkumny zamer (s odkazem do CEZ)

Rok uplatnění

1999

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Surface and coatings technology

ISSN

02578972

e-ISSN

—

Svazek periodika

1

Číslo periodika v rámci svazku

no.^120-12

Stát vydavatele periodika

US - Spojené státy americké

Počet stran výsledku

5

Strana od-do

—

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—