Polypropylene nanocomposites studied by local micro- and nano-mechanical measurements

Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23640%2F11%3A43896512" target="_blank" >RIV/49777513:23640/11:43896512 - isvavai.cz</a>
Výsledek na webu
—
DOI - Digital Object Identifier
—

Jazyk výsledku
angličtina
Název v původním jazyce
Polypropylene nanocomposites studied by local micro- and nano-mechanical measurements
Popis výsledku v původním jazyce
This paper reports on a micro- and nano-indetation investigation of polypropylene nanocomposites filled with multiwall carbon nantubes in the range of 0.1-3 wt.%. Vickers microhardness was determined using microhardness tester. Elastic modulus, instantaneous compliance and hardness were obtained using an nanoindenter. It was established that a small weight fractions of nanotubes (0.1 wt.%) significantly improves the microindentation parameters.
Název v anglickém jazyce
Polypropylene nanocomposites studied by local micro- and nano-mechanical measurements
Popis výsledku anglicky
This paper reports on a micro- and nano-indetation investigation of polypropylene nanocomposites filled with multiwall carbon nantubes in the range of 0.1-3 wt.%. Vickers microhardness was determined using microhardness tester. Elastic modulus, instantaneous compliance and hardness were obtained using an nanoindenter. It was established that a small weight fractions of nanotubes (0.1 wt.%) significantly improves the microindentation parameters.

Druh
J<sub>x</sub> - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)
CEP obor
JJ - Ostatní materiály
OECD FORD obor
—

Rok uplatnění
2011
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Podobné výsledky(10)