The Variation of Mechanical Properties of WC-Based HVOF Sprayed Coatings with Respect to the Co Content
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F49777513%3A23640%2F14%3A43919889" target="_blank" >RIV/49777513:23640/14:43919889 - isvavai.cz</a>
Výsledek na webu
<a href="http://dx.doi.org/10.4028/www.scientificic.net/KEM.586.133" target="_blank" >http://dx.doi.org/10.4028/www.scientificic.net/KEM.586.133</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.4028/www.scientificic.net/KEM.586.133" target="_blank" >10.4028/www.scientificic.net/KEM.586.133</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
The Variation of Mechanical Properties of WC-Based HVOF Sprayed Coatings with Respect to the Co Content
Popis výsledku v původním jazyce
The indentation methods (HR15N, HV0.3, HIT, EIT) were used to evaluate differences between the WC-based coatings with 12, 17 and 25% of Co binder. Two sets of WC-12%Co coatings with two different sets of parameters were sprayed to evaluate the influenceof spraying parameters. Measured mechanical characteristic were correlated to the to the wear resistance of the coatings evaluated by dry sand/rubber wheel test according to ASTM G-65 and pin-on disc according to ASTM G-99. Measured results showed that there is almost no difference between the abrasive wear resistance of WC-Co coating with 12 and 17% of Co binder, while the wear of coating with 25% of Co binder is significantly higher. The importance of the spraying parameters on the WC-12%Co coatings properties was found to be comparable to the importance of binder content influence.
Název v anglickém jazyce
The Variation of Mechanical Properties of WC-Based HVOF Sprayed Coatings with Respect to the Co Content
Popis výsledku anglicky
The indentation methods (HR15N, HV0.3, HIT, EIT) were used to evaluate differences between the WC-based coatings with 12, 17 and 25% of Co binder. Two sets of WC-12%Co coatings with two different sets of parameters were sprayed to evaluate the influenceof spraying parameters. Measured mechanical characteristic were correlated to the to the wear resistance of the coatings evaluated by dry sand/rubber wheel test according to ASTM G-65 and pin-on disc according to ASTM G-99. Measured results showed that there is almost no difference between the abrasive wear resistance of WC-Co coating with 12 and 17% of Co binder, while the wear of coating with 25% of Co binder is significantly higher. The importance of the spraying parameters on the WC-12%Co coatings properties was found to be comparable to the importance of binder content influence.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
JK - Koroze a povrchové úpravy materiálu
OECD FORD obor
—
Návaznosti výsledku
Projekt
<a href="/cs/project/ED2.1.00%2F03.0088" target="_blank" >ED2.1.00/03.0088: Centrum nových technologií a materiálů (CENTEM)</a><br>
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2014
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Key Engineering Materials
ISBN
978-3-03785-876-9
ISSN
1013-9826
e-ISSN
—
Počet stran výsledku
4
Strana od-do
133-136
Název nakladatele
Trans Tech Publications LTD
Místo vydání
Stafa-Zurich
Místo konání akce
Levoca, Slovensko
Datum konání akce
7. 11. 2012
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
—