DEGRADATION SURFACE OF MACHINE SHAFT DUE TO MACHINING TECHNOLOGY

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60162694%3AG43__%2F14%3A00520940" target="_blank" >RIV/60162694:G43__/14:00520940 - isvavai.cz</a>

Výsledek na webu

<a href="http://vavtest.unob.cz/registr" target="_blank" >http://vavtest.unob.cz/registr</a>

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

DEGRADATION SURFACE OF MACHINE SHAFT DUE TO MACHINING TECHNOLOGY

Popis výsledku v původním jazyce

The paper deals with identifying the causes of surface failure of a shaft made of material 42CrMoS4. On the basis of microstructural analysis completed by hardness testing, the occurrence of undesirable phases, such as non-metallic inclusions in the structure of the shaft, can be demonstrated. In the presence of various heterogeneous phases in the material structure, plucking of particles can occur during chip machining which leads to surface damage. In the conclusion, the authors recommend checking thestarting material, which can eliminate problems that cause the degradation of the surface of the shaft. The failure of the surface causes the notch effect which initiates further failures of the material.

Název v anglickém jazyce

DEGRADATION SURFACE OF MACHINE SHAFT DUE TO MACHINING TECHNOLOGY

Popis výsledku anglicky

The paper deals with identifying the causes of surface failure of a shaft made of material 42CrMoS4. On the basis of microstructural analysis completed by hardness testing, the occurrence of undesirable phases, such as non-metallic inclusions in the structure of the shaft, can be demonstrated. In the presence of various heterogeneous phases in the material structure, plucking of particles can occur during chip machining which leads to surface damage. In the conclusion, the authors recommend checking thestarting material, which can eliminate problems that cause the degradation of the surface of the shaft. The failure of the surface causes the notch effect which initiates further failures of the material.

Druh

D - Stať ve sborníku

CEP obor

JQ - Strojní zařízení a nástroje

OECD FORD obor

—

Projekt

—

Návaznosti

S - Specificky vyzkum na vysokych skolach<br>I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název statě ve sborníku

Deterioration, Dependability, Dignostics

ISBN

978-80-7231-969-5

ISSN

—

e-ISSN

—

Počet stran výsledku

10

Strana od-do

39-48

Název nakladatele

Univerzita obrany Brno

Místo vydání

Brno

Místo konání akce

Brno

Datum konání akce

1. 1. 2014

Typ akce podle státní příslušnosti

EUR - Evropská akce

Kód UT WoS článku

—