Technological Degradation of Shaft Surface During Machining

Kód výsledku v IS VaVaI

<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F68407700%3A21220%2F14%3A00222947" target="_blank" >RIV/68407700:21220/14:00222947 - isvavai.cz</a>

Výsledek na webu

—

DOI - Digital Object Identifier

—

Jazyk výsledku

angličtina

Název v původním jazyce

Technological Degradation of Shaft Surface During Machining

Popis výsledku v původním jazyce

The paper deals with identifying the causes of surface failure of a shaft made of material 42CrMoS4. On the basis of microstructural analysis completed by hardness testing, the occurrence of undesirable phases, such as non-metallic inclusions in the structure of the shaft, can be demonstrated. In the presence of various heterogeneous phases in the material structure, plucking of particles can occur during chip machining which leads to surface damage. In the conclusion, the authors recommend checking thestarting material, which can eliminate problems that cause the degradation of the surface of the shaft. The failure of the surface causes the notch effect which initiates further failures of the material.

Název v anglickém jazyce

Technological Degradation of Shaft Surface During Machining

Popis výsledku anglicky

The paper deals with identifying the causes of surface failure of a shaft made of material 42CrMoS4. On the basis of microstructural analysis completed by hardness testing, the occurrence of undesirable phases, such as non-metallic inclusions in the structure of the shaft, can be demonstrated. In the presence of various heterogeneous phases in the material structure, plucking of particles can occur during chip machining which leads to surface damage. In the conclusion, the authors recommend checking thestarting material, which can eliminate problems that cause the degradation of the surface of the shaft. The failure of the surface causes the notch effect which initiates further failures of the material.

Druh

J_x - Nezařazeno - Článek v odborném periodiku (Jimp, Jsc a Jost)

CEP obor

JG - Hutnictví, kovové materiály

OECD FORD obor

—

Projekt

—

Návaznosti

V - Vyzkumna aktivita podporovana z jinych verejnych zdroju

Rok uplatnění

2014

Kód důvěrnosti údajů

S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů

Název periodika

Perner's Contact

ISSN

1801-674X

e-ISSN

—

Svazek periodika

IX

Číslo periodika v rámci svazku

2

Stát vydavatele periodika

CZ - Česká republika

Počet stran výsledku

11

Strana od-do

15-25

Kód UT WoS článku

—

EID výsledku v databázi Scopus

—