Defects in High Entropy Alloy HfNbTaTiZr Prepared by High Pressure Torsion
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F60193247%3A_____%2F17%3AN0000020" target="_blank" >RIV/60193247:_____/17:N0000020 - isvavai.cz</a>
Nalezeny alternativní kódy
RIV/00216208:11320/18:10389663
Výsledek na webu
<a href="http://przyrbwn.icm.edu.pl/APP/PDF/134/app134z3p62.pdf" target="_blank" >http://przyrbwn.icm.edu.pl/APP/PDF/134/app134z3p62.pdf</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.12693/APhysPolA.134.891" target="_blank" >10.12693/APhysPolA.134.891</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Defects in High Entropy Alloy HfNbTaTiZr Prepared by High Pressure Torsion
Popis výsledku v původním jazyce
High entropy alloy HfNbTaTiZr was successfully processed by severe plastic deformation using high pressure torsion (HPT) and ultrafine grained microstructure was achieved. The microstructure of HPT-deformed HfNbTaTiZr alloy was characterized by X-ray diffraction and compared with conventionally cast ingots. The lattice defects introduced by HPT processing were characterized by positron annihilation spectroscopy. The X-ray diffraction profiles of HTP-deformed samples were extremely broadened due to small sizes of coherently diffracting domains and a high microstrain introduced by severe plastic deformation.
Název v anglickém jazyce
Defects in High Entropy Alloy HfNbTaTiZr Prepared by High Pressure Torsion
Popis výsledku anglicky
High entropy alloy HfNbTaTiZr was successfully processed by severe plastic deformation using high pressure torsion (HPT) and ultrafine grained microstructure was achieved. The microstructure of HPT-deformed HfNbTaTiZr alloy was characterized by X-ray diffraction and compared with conventionally cast ingots. The lattice defects introduced by HPT processing were characterized by positron annihilation spectroscopy. The X-ray diffraction profiles of HTP-deformed samples were extremely broadened due to small sizes of coherently diffracting domains and a high microstrain introduced by severe plastic deformation.
Klasifikace
Druh
J<sub>imp</sub> - Článek v periodiku v databázi Web of Science
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
Výsledek vznikl pri realizaci vícero projektů. Více informací v záložce Projekty.
Návaznosti
P - Projekt vyzkumu a vyvoje financovany z verejnych zdroju (s odkazem do CEP)
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název periodika
ACTA PHYSICA POLONICA A
ISSN
0587-4246
e-ISSN
—
Svazek periodika
134
Číslo periodika v rámci svazku
3
Stát vydavatele periodika
PL - Polská republika
Počet stran výsledku
4
Strana od-do
891-894
Kód UT WoS článku
000453257500063
EID výsledku v databázi Scopus
—