Defects in High Entropy Alloy HfNbTaTiZr Prepared by High Pressure Torsion
Identifikátory výsledku
Kód výsledku v IS VaVaI
<a href="https://www.isvavai.cz/riv?ss=detail&h=RIV%2F61389021%3A_____%2F17%3A00507464" target="_blank" >RIV/61389021:_____/17:00507464 - isvavai.cz</a>
Výsledek na webu
<a href="http://przyrbwn.icm.edu.pl/APP/PDF/134/app134z3p62.pdf" target="_blank" >http://przyrbwn.icm.edu.pl/APP/PDF/134/app134z3p62.pdf</a>
DOI - Digital Object Identifier
<a href="http://dx.doi.org/10.12693/APhysPolA.134.891" target="_blank" >10.12693/APhysPolA.134.891</a>
Alternativní jazyky
Jazyk výsledku
angličtina
Název v původním jazyce
Defects in High Entropy Alloy HfNbTaTiZr Prepared by High Pressure Torsion
Popis výsledku v původním jazyce
High entropy alloy HfNbTaTiZr was successfully processed by severe plastic deformation using high pressure torsion (HPT) and ultrafine grained microstructure was achieved. The microstructure of HPT-deformed HfNbTaTiZr alloy was characterized by X-ray diffraction and compared with conventionally cast ingots. The lattice defects introduced by HPT processing were characterized by positron annihilation spectroscopy. The X-ray diffraction profiles of HTP-deformed samples were extremely broadened due to small sizes of coherently diffracting domains and a high microstrain introduced by severe plastic deformation.
Název v anglickém jazyce
Defects in High Entropy Alloy HfNbTaTiZr Prepared by High Pressure Torsion
Popis výsledku anglicky
High entropy alloy HfNbTaTiZr was successfully processed by severe plastic deformation using high pressure torsion (HPT) and ultrafine grained microstructure was achieved. The microstructure of HPT-deformed HfNbTaTiZr alloy was characterized by X-ray diffraction and compared with conventionally cast ingots. The lattice defects introduced by HPT processing were characterized by positron annihilation spectroscopy. The X-ray diffraction profiles of HTP-deformed samples were extremely broadened due to small sizes of coherently diffracting domains and a high microstrain introduced by severe plastic deformation.
Klasifikace
Druh
D - Stať ve sborníku
CEP obor
—
OECD FORD obor
20501 - Materials engineering
Návaznosti výsledku
Projekt
<a href="/cs/project/GA17-17016S" target="_blank" >GA17-17016S: Vliv defektů na vlastnosti biokompatibilních slitin s vysokou entropií</a><br>
Návaznosti
I - Institucionalni podpora na dlouhodoby koncepcni rozvoj vyzkumne organizace
Ostatní
Rok uplatnění
2017
Kód důvěrnosti údajů
S - Úplné a pravdivé údaje o projektu nepodléhají ochraně podle zvláštních právních předpisů
Údaje specifické pro druh výsledku
Název statě ve sborníku
Acta Physica Polonica
ISBN
—
ISSN
0587-4246
e-ISSN
—
Počet stran výsledku
4
Strana od-do
891-894
Název nakladatele
Polish Academy of Sciences
Místo vydání
Varšava
Místo konání akce
Praha
Datum konání akce
10. 9. 2017
Typ akce podle státní příslušnosti
WRD - Celosvětová akce
Kód UT WoS článku
000453257500063